Chromium compounds and uses thereof

ABSTRACT

Novel chromium-containing compounds, such as, for example, chromium pyrrolides, are prepared by forming a mixture of a chromium salt, a metal amide, and an electron pair donor solvent, such as, for example, an ether. These novel chromium-containing, or chromium pyrrolide, compounds can be used either unsupported or supported on an inorganic oxide support to trimerize and/or polymerize olefins.

This application is a divisional application of Ser. No. 07/454,554, filed Dec. 21, 1989 and now abandoned, which is a continuation-in-part of application Ser. No. 07/392,688, filed Aug. 10, 1989, now abandoned.

BACKGROUND OF THE INVENTION

This invention relates to chromium catalysts to trimerize and/or polymerize olefins. This invention also relates to a process to trimerize and/or polymerize olefins.

Supported chromium oxide catalysts have been a dominant factor in the production of olefin polymers, such as polyethylene of copolymers of ethylene and hexane. These catalysts can be used in a variety of polymerization processes. However, most known chromium compounds must be supported to be catalytically active. Furthermore, most supported chromium compounds are useful only for olefin polymerization. If an olefin copolymer is desired, the polymerization process becomes more complex in that two different monomers must be fed to the polymerization reactor.

Olefin trimerization catalysts are also known in the art, but usually lack selectivity to a desired product and also have a low product yield. However, olefin trimerization, if done efficiently, is a process to provide useful olefins, which in turn, can be further trimerized or, optionally, incorporated into a polymerization process.

SUMMARY OF THE INVENTION

Therefore, it is an object of this invention to provide novel chromium compounds.

It is yet another object of this invention to provide a process to prepare at least one novel chromium compound.

It is a further object of this invention to provide an improved process to trimerize olefins.

It is yet another object of this invention to provide a process to polymerize olefins.

It is a further object of this invention to provide an improved olefin trimerization catalyst.

It is yet another object of this invention to provide an olefin polymerization catalyst.

Therefore, in accordance with this invention, novel chromium-containing compounds are prepared from a reaction mixture comprising a chromium salt, a metal amide, and any electron pair donor solvent, such as, for example, an ether.

In accordance with another embodiment of this invention this chromium-containing compound can be used, either supported or unsupported, to trimerize or polymerize olefins.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a computer generated ball and stick projection, with the exception of the chromium atoms which are represented as thermal ellipsoids, or a simplified structural representation or formula, of a molecule of Product I, Cr₅ (NC₄ H₄)₁₀ (OC₄ H₈)₄, as determined by single crystal x-ray crystallography, and

FIG. 2 is a further simplified ball and stick projection, with the exception of the chromium atoms which are represented as thermal ellipsoids, or a structural representation, of the same molecule shown in FIG. 1.

FIG. 3 is a computer generated ORTEP drawing of the structure, or a simplified structural representation or formula, of a molecule of Product III, [Cr(NC₄ H₄)₄ ]⁻², as determined by single crystal x-ray crystallography.

FIG. 4 is a further simplified ball and stick projection, with the exception of the chromium atoms which are represented as thermal ellipsoids, or a structural representation, of the same molecule shown in FIG. 3, however, the entire crystal structure or lattice, with the formula Cr(NC₄ H₄)₄ Na₂.20C₄ H₈ is shown.

FIG. 5 is a computer generated ORTEP drawing of the structure, or a simplified structural representation or formula, of a molecule of Product IV, [Cr(NC₄ H₄)₅ (OC₄ H₈)]⁻², as determined by single crystal x-ray crystallography, and

FIG. 6 is a further simplified ball and stick projection, with the exception of the chromium atoms which are represented as thermal ellipsoids, or a structural representation, of the same molecule shown in FIG. 5, however the entire crystal structure or lattice, with the formula [Cr(NC₄ H₄)₅ (OC₄ H₈)][Na]₂.4(OC₄ H₈), is shown.

FIG. 7 is a computer generated ORTEP drawing of a molecule of Product V, Cr(NC₄ H₄)₃ Cl(O₂ C₂ H₄ (CH₃)₂)₃ Na, which includes the entire crystal structure or lattice, as determined by single crystal x-ray crystallography.

FIG. 8 is a further simplified ball and stick projection of the same molecule shown in FIG. 7.

FIG. 9 is a further simplified ball and stick projection of [Cr(NC₄ H₄)₃ Cl(O₂ C₂ H₄ (CH₃)₂)]⁻¹, with the exception of the chromium atom which is represented as a thermal ellipsoid. This is the same molecule as that shown in FIGS. 7 and 8, however, the entire crystal structure, or lattice is not shown in FIG. 9.

DETAILED DESCRIPTION OF THE INVENTION The Chromium Compounds

The inventive chromium compounds, which can be used preferably for olefin trimerization and, optionally, olefin polymerization, can be produced by forming a reaction mixture comprising a chromium salt, a metal amide, and any electron pair donor solvent, such as, for example, an ether. As used in this disclosure, the inventive chromium compounds are referred to by a variety of interchangeable names, such as inventive or novel chromium compound(s), chromium complex(es), chromium pyrrole complex(es) and/or chromium pyrrolide.

The chromium salt can be one or more organic or inorganic chromium salts, wherein the chromium oxidation state is from 0 to 6. As used in this disclosure, chromium metal is included in this definition of a chromium salt. Generally, the chromium salt will have a formula of CrX_(n), wherein X can be the same or different and can be any organic or inorganic radical, and n is an integer from 1 to 6. Exemplary organic radicals can have from about 1 to about 20 carbon atoms, and are selected from the group consisting of alkoxy, ester, ketone, and/or amido radicals. The organic radicals can be straight-chained or branched, cyclic or acyclic, aromatic or aliphatic, and can be made of mixed aliphatic, aromatic, and/or cycloaliphatic groups. Exemplary inorganic radicals include, but are not limited to halides, sulfates, and/or oxides.

Preferably, the chromium salt is a halide, such as, for example chromous bromide, chromic bromide, chromous iodide, chromic iodide, chromous fluoride, chromic fluoride, chromous chloride, chromic chloride, and mixtures thereof. Most preferably, the chromium salt is a chloride, such as, for example chromous chloride and/or chromic chloride, due to simple separation of the reaction by-products such as, for example, sodium chloride, as well as relatively low cost.

The metal amide can be any metal amide that will react with a chromium salt to form a chromium-amido complex. Broadly, the metal amide can be any heteroleptic or homoleptic metal complex or salt, wherein the amide radical can be any nitrogen-containing organic radical. The metal amide can be either affirmatively added to the reaction, or generated in-situ. Generally, the metal amide will have from about 1 to about 20 carbon atoms. Exemplary metal amides include, but are not limited to, primary and/or secondary amines, any alkali metal (Group IA, and including hydrogen, of the Periodic Table) amide and/or any alkaline earth metal (Group IIA of the Periodic Table) amide. The hydrocarbyl portion of the salt of the metal amide is selected from the group consisting of straight chain or branched, cyclic or acyclic, aromatic or aliphatic, and mixtures of two or more thereof. Preferably, the metal amide is selected from a Group IA, and including hydrogen, or Group IIA metal amide, due to ease of reaction with chromium halides.

Exemplary preferred metal amides include, but are not limited to, lithium dimethylamide, lithium diethylamide, lithium diisopropylamide, lithium dicyclohexylamide, sodium bis(trimethylsilyl)amide, sodium indolide, sodium pyrrolide, and mixtures of two or more thereof. Most preferably, the metal amide is a pyrrolide. As used in this disclosure, a pyrrolide is defined as a compound comprising a 5-membered, nitrogen-containing heterocycle, such as, for example, pyrrole, derivatives of pyrrole, and mixtures thereof. Exemplary pyrrolides are selected from the group consisting of hydrogen pyrrolide (pyrrole), lithium pyrrolide, sodium pyrrolide, potassium pyrrolide, cesium pyrrolide, and/or the salts of substituted pyrrolides, because of high reactivity and activity with the other reactants. Examples of salts of substituted pyrrolides include, but are not limited to sodium 2,5-dimethyl pyrrolide and/or 3,4-dimethyl pyrrolide. When the metal amide is a pyrrolide ligand, the resultant chromium compound is a chromium pyrrolide.

The electron pair donor solvent can be any electron pair donor solvent to affect a reaction between the chromium salt and the metal amide. While not wishing to be bound by theory, it is believed that the electron pair donor solvent can be a reaction solvent, as well as a possible reactant. Exemplary electron pair donor solvents include, but are not limited to, nitrogen-, oxygen-, phosphorous-, and/or sulfur-containing compounds and/or ethers.

Exemplary nitrogen-containing compounds include, but are not limited to nitriles, such as, for example, acetonitrile; amines, such as, for example, pyridine, and/or amides. Additional exemplary nitrogen-containing compounds include, but are not limited to, nitromethane, dimethylpyridine, dimethylformamide, N-methylformamide, aniline, nitrobenzene, tetramethyldiaminomethane, hexamethyldisilazane, and/or pyrrolidone.

Exemplary oxygen-containing compounds include, but are not limited to, acetone, ethyl acetate, methyl acetate, methanol, ethanol, ethyl methyl ketone, acetaldehyde, furan, and/or hexamethyldisiloxane.

Exemplary phosphorous-containing compounds include, but are not limited to, hexamethylphosphoramide, hexamethylphosphorous triamide, triethylphosphite, tributylphosphine oxide, and/or triethylphosphine.

Exemplary sulfur-containing compounds include, but are not limited to, carbon disulfide, dimethylsulfoxide, tetramethylene sulfone, triophene, and/or dimethylsulfide or mixtures thereof.

The ether in the reaction mixture can be one or more ether compounds to affect a reaction between the chromium salt and the metal amide. While not wishing to be bound by theory, it is believed that the ether can be a reaction solvent, as well as a possible reactant. The ether can be any aliphatic and/or aromatic compound containing an R--O--R functionality, wherein the R groups can be the same or different, but preferably is not hydrogen. Preferred ethers are aliphatic ethers, for safety reasons in that aromatic ethers are human toxins. Furthermore, the preferred ethers are those which facilitate a reaction between a chromium halide and a Group IA or Group IIA metal pyrrolide, and also can be easily removed from the reaction mixture. Exemplary compounds include, but are not limited to, tetrahydrofuran, dioxane, diethylether, dimethoxyethane (glyme), diglyme, triglyme, and mixtures of two or more dimethoxyethane (glyme), diglyme, triglyme, and mixtures of two or more thereof. Most preferably, the ether is selected from the group consisting of tetrahydrofuran, derivatives of tetrahydrofuran, dimethoxyethane, derivatives of dimethoxyethane, and mixtures thereof, for the reasons given above, as well as the reason that the preferred salt of an amine in soluble in these ethers.

The amount of each reactant used to prepared one or more of the novel chromium compounds can vary, based on the desired chromium compound product. Any amount of each reactant can be used to produce the novel chromium compounds, depending on the desired product. Different reaction stoichiometries can produce different chromium compounds. For example, the reaction of about one mole of chromium (II) with about two moles of sodium pyrrolide can produce different products than reacting about one mole of chromium (II) with an excess of sodium pyrrolide. Furthermore, as stated earlier, selection of different, although similar reactants, can produce different products. For example, using either tetrahydrofuran or dimethoxyethane can result in a different reaction product.

The three reactants can be combined in any manner under conditions suitable to form a solution comprising one or more of the inventive chromium compounds. The reaction preferably occurs in the absence of oxygen and therefore under an inert, such as, for example, nitrogen and/or argon. The reaction pressure can be any pressure sufficient to maintain the reactants in a liquid state. Generally, pressure within the range of from about atmospheric pressure to about three atmospheres are acceptable. For ease of operation atmospheric pressure is generally employed.

The reaction temperature can be any temperature which maintains the ether in a liquid form. In order to effectuate a more efficient reaction, temperatures near the boiling point of the ether are preferred. Most preferably, the reaction temperature is at the boiling point of the ether and the reaction mixture is refluxed for a period of time.

The reaction time can be any amount of time necessary for the reaction to occur. Depending on the reactants, as well as the reaction temperature and pressure, reaction time can vary from about 1 minute to about 1 week. Usually, reaction time ranges from about 3 hours to about 5 days. Under optimum conditions, the reaction time can be within the range of from about 3 to about 48 hours.

After the reaction is complete, a solid reaction product can be recovered by any method known in the art. Preferably, though not required, upon completion of the reaction, the reaction mixture first is filtered to remove any reaction insoluble by-products such as, for example, salts, like sodium chloride, prior to any other treatment. Although removal of any reaction by-products is not necessary, such removal preferably is done in order to expedite later purification of the chromium product. After filtering, one exemplary method to recover a solid reaction product is to remove the excess ether from the reaction mixture. The excess electron pair donor solvent, such as, for example an ether, can be removed according to any method known in the art. Exemplary electron pair donor solvent, such as, for example an ether, removal methods include, but are not limited to, slow evaporation, under vacuum and/or a nitrogen purge.

Other electron pair donor solvent, such as, for example an ether, removal procedures can be used either alone or in combination. For example, the reaction mixture can be filtered and then vacuum dried. Preferably, the reaction mixture is heated slowly and maintained at temperature within the range of about 10° C. to about 300° C., preferably about 25° C. to about 200° C., under a vacuum, for safety, to remove the excess electron pair donor solvent, such as, for example an ether. The resultant solid reaction product is one or more of the inventive chromium compounds.

Alternatively, the reaction mixture can be filtered to remove any solid reaction by-product solids and the filtered reaction mixture can be contacted with a non-polar organic solvent. Addition of a non-polar organic solvent causes one or more of the inventive chromium compounds to form a solid precipitate. Exemplary non-polar organic solvent include, but are not limited to, pentane, hexane, cyclohexane, heptane, and mixtures thereof. Most preferably pentane is added to the filtered reaction mixture because of the availability and ease of use.

The precipitated inventive chromium compounds can be recovered by any method known in the art. The simplest procedure to recover the inventive precipitated chromium compounds is by filtration.

The reaction mixture and the resultant solid reaction products, as stated earlier, are kept in an oxygen-free atmosphere at all times. Preferably, due to availability and ease of use, an inert atmosphere such as, for example, nitrogen, is the ambient.

Numerous chromium compounds can be prepared in accordance to the invention, by varying the reactants and/or the quantity of each reactant employed. The recovered, novel chromium compound or compounds can be used for olefin trimerization and/or polymerization without further purification.

Optionally, the chromium compound can be purified in accordance with any method known in the art. For example, one of the simplest purification procedures is to wash the recovered solid with a non-polar organic solvent such as, for example, toluene. Preferably, a non-polar aliphatic organic solvent is used for best results. Exemplary wash solvents include, but are not limited to, pentane, hexane, cyclohexane, heptane, and mixtures thereof. Most preferably, pentane is the wash solvent.

The inventive chromium compounds can be used as a supported and/or unsupported catalyst for olefin trimerization and/or polymerization. A supported chromium catalyst can be prepared according to any method known in the art. Any support useful to support chromium catalyst can be used. Exemplary catalyst supports include, but are not limited to, inorganic oxides, either alone or in combination, phosphated inorganic oxides, and mixtures thereof. Particularly preferred are supports selected from the group consisting of silica, silica-alumina, alumina, fluorided alumina, silated alumina, thoria, aluminophosphate, aluminum phosphate, phosphated silica, phosphated alumina, silica-titania, coprecipitated silica/titania, and mixtures, thereof, fluorided/silated alumina, being presently preferred, as well as any one or more of these supports which can contain chromium. The presently most preferred catalyst support is because of the greatest trimerization activity, is aluminophosphate, as disclosed in U.S. Pat. No. 4,364,855 (1982), herein incorporated by reference.

The supported chromium catalyst system can be prepared according to any method known in the art. For example, the reaction mixture, which preferably has been filtered to remove any particulate reaction by-products and contains one or more of the novel chromium pyrrolide compounds, is combined and thoroughly contacted with a catalyst support. Excess electron pair donor solvent, such as, for example an ether, does not have to be removed prior to contacting the catalyst support. However, a solid chromium pyrrolide compound can be re-dissolved in an electron pair donor solvent, such as, for example an ether, if desired. The chromium pyrrolide/ether solution is usually a blue or blue/green color, although other colors can be observed.

The catalyst support usually is insoluble in the ether/chromium pyrrolide complex solution. Any excess of the chromium pyrrolide in relation to the catalyst support is sufficient. However, usually, at least about 5 grams of chromium pyrrolide compound per gram of catalyst support is sufficient. Preferably about 0.001 to about 1 grams of chromium pyrrolide compound per gram of support, and most preferably about 0.01 to about 0.5 grams of chromium pyrrolide compound per gram of support is used for best support loading and most efficient use of the reagents. This mixture can be contacted and mixed at any time, temperature, and pressure to thoroughly contact the chromium pyrrolide compound and support. For ease of use, ambient temperatures and pressures are preferred. Mixing times can be up to about 24 hours, preferably about 5 seconds to about 10 hours, and most preferably about 5 seconds to about 8 hours. Longer times usually provide no additional benefit and shorter times can be insufficient for thorough contacting.

After the support is added and thoroughly combined with the chromium pyrrolide it is collected by filtration, vacuum dried, then an activating compound, usually as a solution of one or more Lewis acids and/or metal alkyls, preferably in a hydrocarbon solvent, is added to the support/chromium pyrrolide mixture. As used in this disclosure, a Lewis acid is defined as any compound that is an electron acceptor. Preferably, the activating compound is a compound that can be considered both a Lewis acid and a metal alkyl. Preferred activating compounds which are both a metal alkyl and a Lewis acid include, but are not limited to, alkylaluminum compounds, and mixtures thereof. The most preferred alkylaluminum compound is triethylaluminum, for best results in catalyst activity.

The hydrocarbon solvent can be any hydrocarbon that will dissolve the Lewis acid. Preferred hydrocarbons include, but are not limited to, aromatic compounds having from about 6 to about 50 carbon atoms per molecule. Most preferably, the hydrocarbon solvent is toluene, for ease of removal and minimal interference with the resultant catalyst.

Any amount of activating compounds, such as a metal alkyl and/or a Lewis acid is sufficient to activate and/or react with the chromium pyrrolide catalyst. Usually about 200 grams of Lewis acid per gram of chromium can be used. Preferably, about 1 to about 100 grams of activating compound, such as a metal alkyl and/or a Lewis acid per gram of chromium pyrrolide, and most preferably about 5 to about 30 grams of activating compound, such as a metal alkyl and/or a Lewis acid per gram of chromium pyrrolide are used, for best catalyst activity. However, the amount of Lewis acid employed can vary with the catalyst support used. For example, if the support is silica and/or alumina, too much activating compound, such as a metal alkyl and/or a Lewis acid can decrease catalyst activity. However, a similar amount of activating compound, such as a metal alkyl and/or a Lewis acid used with an aluminophosphate support does not always significantly decrease catalyst activity.

As disclosed earlier, the mixture of chromium pyrrolide, catalyst support, and activating compound, such as a metal alkyl and/or a Lewis acid are mixed and/or contacted under a dry, inert atmosphere at all times. Any pressure can be used during the contacting; for ease of use, atmospheric pressure is preferred. Any temperature can be used during the contacting; for ease of use, room temperature, or ambient temperature, is preferred. Some care should be taken during the mixing, so as not to destroy the physical integrity of the chromium pyrrolide, catalyst support, and resultant supported catalyst. The three-component mixture can be contacted for any amount of time sufficient to prepare and activate a chromium catalyst. Usually times in the the range of about one minute to about one week are sufficient. Preferably, times in the range of about 30 minutes to about 24 hours are used, and most preferably times in the range of about one hour to about 12 hours are used. Too short of mixing times can result in incomplete contacting and too long of mixing times will not provide any additional catalytic benefit.

An alternative, and presently preferred, method to produce a supported catalyst is to combine one or more solid, inventive chromium pyrrolide compounds with a hydrocarbon solvent, a disclosed earlier, such as, for example, toluene, and an activating compound, such as a metal alkyl and/or a Lewis acid, as disclosed earlier, such as, for example, triethylaluminum. This mixture can be stirred for any time sufficient to dissolve the chromium pyrrolide compound, at any pressure or temperature. Usually, times of about one minute to about one week, preferably about one hour to about 24 hours, and most preferably within the range of about three hours to about 12 hours are used. For ease of operation, ambient temperatures and pressures are used. Usually, a brown solution will result.

After the solution is sufficiently mixed, a support is added to the solution and stirred to thoroughly contact the solution and support. The quantity of support is any amount sufficient to support the chromium pyrrolide compound. Generally, the amount of support necessary is the same as that disclosed in the previous ememplary process. Any suitable pressure and temperature can be used, although ambient temperature and pressure are preferred for ease of use. Usually, the mixing and/or contacting time is within the range of about 30 minutes to about one week, preferably from about 3 hours to about 48 hours. Most preferably, the mixing and/or contacting time is within the range of about 5 hours to about 24 hours, to maximize efficiency and result in a thoroughly contacted support.

The solution then can be filtered to recover a solid catalytic product. The catalytic product, as with the reactants and reactions, is preferably kept under an inert atmosphere to maintain chemical stability.

If the chromium compound, such as, for example, a chromium pyrrolide, is recovered and is to be used as an unsupported trimerization and/or polymerization catalyst, olefins can be trimerized or polymerized in a presence of one or more of the inventive homogeneous chromium compounds, a saturated hydrocarbon as a diluent, and Lewis acid. Optionally, hydrogen can be added to the reactor to accelerate the reaction.

Reactants

Reactants applicable for use in polymerization with the catalyst and processes of this invention are olefinic compounds which can polymerize, i.e., react the same or with other olefinic compounds. Catalyst of the invention can be used to polymerize at least one linear or branched mono-1-olefin having about 2 to about 8 carbon atoms. Exemplary compounds include, but are not limited to, ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 1-octene, and mixtures thereof.

Reactants applicable for use in the trimerization process, i.e., the combination of any three olefins, of this invention are olefinic compounds which can a) self-react, i.e., trimerize, to give useful products such as, for example, the self reaction of ethylene can give one hexene; and/or b) olefinic compounds which can react with other olefinic compounds, i.e., co-trimerize, to give useful products such as, for example, co-trimerization of ethylene plus hexene can give one decene and/or 1-tetradecene, co-trimerization of ethylene and 1-butene gives one octene, or 1-decene and ethylene can give 1-tetradecene and/or 1-docosene. As used herein, the term "trimerization" is intended to include "co-trimerization" as defined above.

Suitable trimerizable olefinic compounds are those compounds having from about 2 to about 30 carbon atoms per molecule and having at least one olefinic double bond. Exemplary compounds include, but are not limited to acyclic and cyclic olefins such as, for example, ethylene, propylene, 1-butene, 2-butene, isobutylene, 1-pentene, 2-pentene, 1-hexene, 2-hexene, 3-hexene, 1-heptene, 2-heptene, 3-heptene, the four normal octenes, the four normal nonenes, and mixtures of any two or more thereof. If branched and/or cyclic olefins are used as reactants, while not wishing to be bound by theory, it is believed that steric hindrance could hinder the trimerization process. Therefore, the branched and/or cyclic portion(s) of the olefin should be distant from the carbon-carbon double bond.

The reaction products, i.e., trimers and/or polymers, can be prepared from the catalyst systems of this invention by solution reactions, slurry reactions, and/or gas phased reaction techniques using conventional equipment and contacting processes. Contacting of the monomer or monomers with the catalyst system can be effected by any manner known in the art of solid catalyst. One convenient method is to suspend the catalyst system in an organic medium and to agitate the mixture to maintain the catalyst system in suspension throughout the trimerization and/or polymerization process. Other known contacting methods such as fluidized bed, gravitating bed, and fixed bed can also be employed. Optionally, hydrogen can be added to the reactor to accelerate the reaction.

The catalyst systems of this invention are particularly suitable for use in slurry trimerization and/or polymerizations. The slurry process is generally carried out in an inert diluent (medium), such as a paraffin, cycloparaffin, or aromatic hydrocarbon. One exemplary reactor diluent is isobutane. When the reactant is predominately ethylene, a temperature in the range of about 60° to about 110° C. is employed.

Products

The olefinic and/or polymeric products of this invention have established utility in a wide variety of applications such as, for example, as monomers for use in the preparation of homopolymers, copolymers, and/or terpolymers. The polymeric products of this invention have established utility in a wide variety of applications such as for example, polyethylene.

The further understanding of the present invention and its advantages will be provided by reference to the following examples.

EXAMPLES Preparation of Chromium-Containing Compounds

Manipulations of all reactants were carried out either in a drybox employing nitrogen, or in airless glassware employing vacuum or nitrogen. Tetrahydrofuran (THF), toluene, benzene, diethylbenzene (Aldrich, 97% mixture of 1,2-, 1,3-, 1,4- isomers) and pentane were purified by distillation over sodiumbenzophenone ketyl under nitrogen, then degassed via a nitrogen purge. Dimethoxyethane (DME) (Aldrich, anhydrous) was degassed via nitrogen purge and used without further purification. Pyrrole (Aldrich, 98%) was vacuum distilled over sodium, then degassed via nitrogen purge. 2,5-Dimethylpyrrole was dried with calcium sulfate and vacuum distilled. Sodium 2,5-dimethylpyrrolide (NaC₆ H₈ N) was prepared by reacting 2,5-dimethylpyrrole with an excess of sodium (40% by weight dispersion in mineral spirits) in refluxing tetrahydrofuran under nitrogen. Sodium pyrrolide was prepared by reacting pyrrole with an equivalent molar amount (1:1) of NaH (Aldrich, 60% by weight in mineral oil) or sodium (40% dispersion by weight in mineral spirits) in dimethoxyethane or tetrahydrofuran (THF) at ambient temperature under nitrogen. Triethylaluminum (TEA) (Aldrich 1.0M, hexanes and 1.9M toluene) was used as received. Ketjen Grade B alumina (Al₂ O₃) and Davison 952 silica (SiO₂) were the commercial materials used as supports for catalyst preparations. Fluorided-alumina (F/Al₂ O₃, 15 wt % F) was prepared by the addition of a solution of NH₄ HF₂ in methanol to Ketjen Grade B alumina. Phosphated silica (P/SiO₂, P/Si molar ratio=0.1) was prepared by the addition of a 10% H₃ PO₄ /methanol solution to Davison 952 silica. The aluminophosphate (AlPO₄) used in the following experiments was made as described in McDaniel et al, U.S. Pat. No. 4,364,855 (1982). The supports were activated by placing up to 25 g into a fritted quartz tube, fluidizing with air and calcining at 700° C., except for P/SiO₂ at 350° C., for 3 hours. The air stream was switched to nitrogen until the support cooled to ambient temperature.

Chromium pyrrolide complexes were typically prepared from anhydrous chromium (II or III) chloride and sodium pyrrolide as follows:

A typical synthetic procedure useful to prepare chromium pyrrolide complexes was that of reacting the chromium chlorides with sodium pyrrolide (NaC₄ H₄ N, also referred to as NaPy) in refluxing tetrahydrofuran (THF). A molar reactant stoichiometry of 1CrCl₂ and 2NaPy resulted in the isolation of a polymeric material, Product II, as the major product and a pentanuclear complex, Product I, (Cr₅ (NC₄ H₄)₁₀ (OC₄ H₈)₄), as the minor product, see Equation 1. Using molar excess of NaPy resulted in the isolation of the dianionic square planar complex {Cr(NC₄ H₄)₄ }{Na}₂.20C₄ H₈, Product III, and the octahedral complex {Cr(C₄ H₄ N)₅ (OC₄ H₈)}{Na}₂.40C₄ H₈, Product IV, see Equation 2. Each of the products was isolated through precipitation, Product II, or crystallization, Products I, III, IV, from THF solutions by the addition of pentane. ##STR1##

EXAMPLE I

To prepare the pentanuclear complex, Product I, (Cr₅ (NC₄ H₄)₁₀ (OC₄ H₈)₄), and the polymeric material, Product II, chromous chloride (2.0 g/16.27 mmole) was combined with sodium pyrrolide (33.68 mmole) in tetrahydrofuran and refluxed 20 hours. The reaction mixture was filtered (medium porosity frit) and the filtrate was used for fractional crystallization of both (Cr₅ (NC₄ H₄)₁₀ (OC₄ H₈)₄), Product I, and the polymeric material, Product II, through the addition of pentane. The polymeric material crystallized as a blue solid followed by (Cr₅ (NC₄ H₄)₁₀ (OC₄ H₈)₄) as opaque dark blue/purple crystals.

Analysis calculated for C₅₆ H₇₂ N₁₀ Cr₅, Product I: C, 55.62; H, 6.00; N, 11.58%, by weight. Found: C, 55.46; H, 6.32; N, 11.15%, by weight. Analysis found for Product II: Cr, 11.5; C, 59.75; H, 7.61; N, 9.17%, by weight, but variable upon precipitation conditions. An x-ray crystal structure of Product I showed a pentanuclear complex incorporating bridging amido-pyrrolyl, terminal amido-pyrrolyl, and tetrahydrofuran ligands (FIGS. 1 and 2).

EXAMPLE II

To prepare {Cr(NC₄ H₄)₄ }{Na}₂.20C₄ H₈, Product III, and {Cr(C₄ H₄ N)₅ (OC₄ H₈)}{Na}₂.40C₄ H₈, Product IV, chromous chloride (3.0 g/24.4 mmole) was combined with sodium pyrrolide (100.9 mmole) in tetrahydrofuran and refluxed 2 hours, see Equation 2. The reaction mixture was filtered (medium porosity frit) and the filtrate was used for fractional crystallization of both {Cr(NC₄ H₄)₄ }{Na}₂.20C₄ H₈, Product III, and {Cr(C₄ H₄ N)₅ (OC₄ H₈)}{Na}₂.40C₄ H₈, Product IV, through the addition of pentane. Product III crystallized as translucent orange/red crystals followed by Product IV as translucent purple crystals. While not wishing to be bound by theory, the formation of Product IV is believed to result from the presence of chromic chloride in the chromous chloride reagent (Alfa, chromium (II) chloride, anhydrous, contains 5-10% by weight CrCl₃) used in the preparation.

Analysis calculated for C₂₄ H₃₂ N₄ O₂ CrNa₂, Product III: C, 56.94; H, 6.32; N, 11.07% by weight. Found: C, 57.04; H, 6.30; N, 10.92%, by weight. Analysis calculated for C₄₀ H₆₀ N₅ O₅ CrNa₂, Product IV: C, 60.90; H, 7.67; N, 8.88% by weight. Found: C, 60.81; H, 7.74; N, 9.44%, by weight. An x-ray crystal structure of Product III showed a square planar complex incorporating terminal amido-pyrrolyl ligands (FIG. 4). An x-ray crystal structure of Product IV showed an octahedral complex incorporating terminal amido-pyrrolyl and a tetrahydrofuran ligand (FIGS. 5 and 6).

EXAMPLE III

The reaction product obtained from sodium pyrrolide and CrCl₃ was the most preferred in the preparation of an active catalyst. Pyrrole (7.0 ml/100.9 mmole) was mixed with NaH (4.2 g of 60%, about 105 mmole) in dimethoxyethane at ambient temperature until bubbling ceased. Chromic chloride (5.33 g/33.7 mmole) was added to the solution at ambient temperature. The reaction mixture was refluxed under nitrogen for five hours, see Equation 3. This resulted in a dark green solution. The solution was filtered (medium porosity frit) and stripped of solvent under vacuum and pumped dry under vacuum for 12 hours. The resultant chromium pyrrolide complex was a green solid, Product V. It was used in the preparation of an active catalyst without further purification. ##STR2##

EXAMPLE IV

All single crystal x-ray structure analyses were performed by Crystalytics Company, Lincoln, Nebr. Examples IV, V, VI, and IX contain the resultant analytical and subsequently computer-generated data.

A single crystal x-ray structure was obtained for [Cr₅ (NC₄ H₄)₁₀ (OC₄ H₈)₄ ], Product I, and shown in FIGS. 1 and 2. The description of the single-crystal sample and amounting used for data collection are as follows:

Color: Dark blue

Shape: Rectangular parallelepiped

Dimensions: 0.20×0.48×0.80 mm

Crystal Mount: Crystal was sealed inside a thin-walled glass capillary with epoxy under N₂.

Crystal Orientation: Crystal was oriented with its longest edge nearly parallel to the phi axis of the diffractometer.

Width at half-height from ω Scans: 0.38°

The space group and cell data are as follows:

Crystal System: Triclinic₋₁

Space Group and Number:² Pl--C_(i) (No. 2)

Number of Computer-Centered Reflections Used in the Least-Squares Refinement of the Cell Dimensions:

15 20°>25° °C.=20°±1°

    ______________________________________                                         Lattice Constants with esd's:                                                  ______________________________________                                         a = 10.803(2)Å                                                                          α = 85.59(2)°                                                                  V = 1407.9(6)Å.sup.3                             b = 9.825(2)Å                                                                           β = 96.23(2)°                                                                   Z = 1                                                c = 14.212(4)Å                                                                          γ = 109.99(2)°                                                                 λ = 0.71073Å                              ______________________________________                                    

Molecular Weight: 1209.24 amu

Calculated Density: 1.427 g/cm⁻¹

Linear Absorption Coefficient:^(3a) 0.96 mm⁻¹

Tables I-V list the resultant parameters used to generate the molecular structures shown in FIGS. 1 and 2.

                  TABLE I                                                          ______________________________________                                         Atomic Coordinates for Nonhydrogen Atoms in                                    Crystalline [Cr.sub.5 (NC.sub.4 N.sub.4).sub.10 (OC.sub.4 H.sub.8).sub.4       ].sup.a                                                                                                  Equivalent Isotropic                                 Atom   Fractional Coordinates                                                                            Thermal Parameter,                                   Type.sup.b                                                                           10.sup.4 x                                                                               10.sup.4 y                                                                              10.sup.4 z                                                                            B, Å.sup.2 × 10.sup.c                ______________________________________                                         Cr.sub.1                                                                             0.sup.d   0.sup.d  0/.sup.d                                                                              25(1)                                          Cr.sub.2                                                                             636(1)    2281(1)  1500(1)                                                                               24(1)                                          Cr.sub.3                                                                             -1179(1)  841(1)   3122(1)                                                                               28(1)                                          N.sub.1a                                                                             -1155(3)  935(3)   715(2) 25(1)                                          C.sub.1a                                                                             -2195(4)  64(4)    1231(3)                                                                               31(1)                                          C.sub.2a                                                                             -3313(4)  390(5)   965(3) 41(1)                                          C.sub.3a                                                                             -3014(4)  1486(5)  257(3) 43(1)                                          C.sub.4a                                                                             -1728(4)  1791(4)  116(3) 34(1)                                          N.sub.1b                                                                             1566(3)   1902(3)  331(2) 29(1)                                          C.sub.1b                                                                             1753(4)   3095(4)  -308(3)                                                                               36(1)                                          C.sub.2b                                                                             3035(5)   3751(5)  -432(3)                                                                               51(2)                                          C.sub.3b                                                                             3736(4)   2986(5)  131(3) 51(2)                                          C.sub.4b                                                                             2823(4)   1865(4)  587(3) 38(1)                                          N.sub.1c                                                                             -320(3)   2997(3)  2480(2)                                                                               27(1)                                          C.sub.1c                                                                             375(4)    3732(4)  3273(3)                                                                               34(1)                                          C.sub.2c                                                                             29(5)     4919(4)  3383(3)                                                                               43(1)                                          C.sub.3c                                                                             -908(5)   4967(4)  2631(3)                                                                               42(1)                                          C.sub.4c                                                                             -1105(4)  3809(4)  2101(3)                                                                               32(1)                                          N.sub.1d                                                                             443(3)    350(3)   2743(2)                                                                               28(1)                                          C.sub.1d                                                                             1600(4)   715(4)   3289(3)                                                                               36(1)                                          C.sub.2d                                                                             2321(4)   -133(5)  3102(3)                                                                               46(2)                                          C.sub.3d                                                                             1567(5)   -1070(5) 2403(3)                                                                               46(2)                                          C.sub.4d                                                                             422(4)    -763(4)  2203(3)                                                                               36(1)                                          N.sub.1e                                                                             -1972(3)  -1122(3) 3801(2)                                                                               35(1)                                          C.sub.1e                                                                             -1344(5)  -2107(4) 4069(3)                                                                               41(1)                                          C.sub.2e                                                                             -2189(5)  -3307(4) 4503(3)                                                                               44(1)                                          C.sub.3e                                                                             -3361(5)  -3061(4) 4531(3)                                                                               47(1)                                          C.sub.4e                                                                             -3206(5)  -1731(4) 4097(3)                                                                               47(1)                                          O.sub.1f                                                                             2351(3)   3985(3)  1883(2)                                                                               32(1)                                          C.sub.1f                                                                             3536(4)   4018(4)  2483(3)                                                                               43(1)                                          C.sub.2f                                                                             4470(6)   5479(6)  2336(5)                                                                               76(2)                                          C.sub.3f                                                                             3642(5)   6408(5)  2147(4)                                                                               62(2)                                          C.sub.4f                                                                             2396(4)   5463(4)  1635(3)                                                                               40(1)                                          O.sub.1g                                                                             -2551(3)  1543(3)  3659(2)                                                                               35(1)                                          C.sub.1g                                                                             -3763(4)  1733(5)  3232(3)                                                                               44(1)                                          C.sub.2g                                                                             -4097(5)  2625(6)  3907(4)                                                                               57(2)                                          C.sub.3g                                                                             -3524(5)  2241(6)  4845(3)                                                                               57(2)                                          C.sub.4g                                                                             -2319(5)  1977(6)  4633(3)                                                                               50(2)                                          ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIG. 1.                             .sup.c This is onethird of the trace of the orthogonalized B.sub.ij            tensor.                                                                        .sup.d This is a symmetryrequired value and is therefore listed without a      estimated standard deviation.                                            

                  TABLE II                                                         ______________________________________                                         Anisotropic Thermal Parameters for Nonhydrogen                                 Atoms in Crystalline [Cr.sub.5 (NC.sub.4 N.sub.4).sub.10 (OC.sub.4             H.sub.8).sub.4 ].sup.a,b                                                       Atom   Anisotropic Thermal Parameter (Å.sup.2 × 10)                  Type.sup.c                                                                           B.sub.11                                                                               B.sub.22                                                                               B.sub.33                                                                             B.sub.12                                                                              B.sub.13                                                                              B.sub.23                             ______________________________________                                         Cr.sub.1                                                                             20(1)   23(1)   32(1) 5(1)   5(1)   -4(1)                                Cr.sub.2                                                                             23(1)   22(1)   27(1) 7(1)   3(1)   -2(1)                                Cr.sub.3                                                                             27(1)   26(1)   34(1) 11(1)  8(1)   1(1)                                 N.sub.1a                                                                             21(1)   27(1)   29(1) 8(1)   1(1)   -2(1)                                C.sub.1a                                                                             28(2)   31(2)   30(2) 4(1)   8(1)   -4(1)                                C.sub.2a                                                                             23(2)   49(2)   49(2) 8(2)   5(2)   -16(2)                               C.sub.3a                                                                             31(2)   51(2)   52(2) 22(2)  -7(2)  -11(2)                               C.sub.4a                                                                             36(2)   32(2)   34(2) 15(1)  -2(1)  -3(1)                                N.sub.1b                                                                             24(1)   25(1)   35(1) 3(1)   5(1)   -4(1)                                C.sub.1b                                                                             40(2)   31(2)   33(2) 2(1)   11(1)  -1(1)                                C.sub.2b                                                                             46(2)   42(2)   54(2) -7(2)  24(2)  -5(2)                                C.sub.3b                                                                             25(2)   50(2)   71(3) -3(2)  15(2)  -27(2)                               C.sub.4b                                                                             29(2)   38(2)   48(2) 10(1)  0(2)   -15(2)                               N.sub.1c                                                                             28(1)   25(1)   30(1) 11(1)  3(1)   -2(1)                                C.sub.1c                                                                             36(2)   35(2)   31(2) 10(1)  4(1)   -3(1)                                C.sub.2c                                                                             52(2)   34(2)   43(2) 13(2)  6(2)   -13(1)                               C.sub.3c                                                                             51(2)   31(2)   50(2) 22(2)  5(2)   -5(2)                                C.sub.4c                                                                             35(2)   34(2)   31(2) 16(1)  4(1)   1(1)                                 N.sub.1d                                                                             32(1)   23(1)   31(1) 12(1)  6(1)   3(1)                                 C.sub.1d                                                                             33(2)   32(2)   42(2) 9(1)   6(2)   -0(1)                                C.sub.2d                                                                             36(2)   50(2)   59(2) 24(2)  6(2)   11(2)                                C.sub.3d                                                                             61(3)   44(2)   47(2) 36(2)  11(2)  3(2)                                 C.sub.4d                                                                             49(2)   35(2)   31(2) 23(2)  4(2)   1(1)                                 N.sub.1e                                                                             36(2)   30(1)   42(2) 13(1)  14(1)  4(1)                                 C.sub.1e                                                                             46(2)   36(2)   46(2) 20(2)  10(2)  6(2)                                 C.sub.2e                                                                             64(3)   30(2)   37(2) 15(2)  7(2)   4(1)                                 C.sub.3e                                                                             55(3)   31(2)   46(2) -1(2)  18(2)  -0(2)                                C.sub.4e                                                                             39(2)   38(2)   62(2) 9(2)   17(2)  4(2)                                 O.sub.1f                                                                             29(1)   25(1)   40(1) 6(1)   -1(1)  -2(1)                                C.sub.1f                                                                             34(2)   44(2)   45(2) 9(2)   -8(2)  -6(2)                                C.sub.2f                                                                             45(3)   67(3)   95(4) -3(2)  -15(3) -6(3)                                C.sub.3f                                                                             59(3)   34(2)   78(3) -2(2)  -6(3)  -9(2)                                C.sub.4f                                                                             45(2)   23(1)   48(2) 7(1)   6(2)   -1(1)                                O.sub.1g                                                                             34(1)   41(1)   37(1) 19(1)  7(1)   -1(1)                                C.sub.1g                                                                             31(2)   56(2)   50(2) 20(2)  4(2)   -5(2)                                C.sub.2g                                                                             47(3)   65(3)   72(3) 35(2)  2(2)   -12(2)                               C.sub. 3g                                                                            60(3)   75(3)   50(2) 36(2)  16(2)  -8(2)                                C.sub.4g                                                                             45(2)   77(3)   35(2) 27(2)  8(2)   -5(2)                                ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b The form of the anisotropic thermal parameter is given in referenc      8 on page 6 of the structure report.                                           .sup.c Atoms are labeled in agreement with FIG. 1.                       

                  TABLE III                                                        ______________________________________                                         Atomic Coordinates for Hydrogen Atoms in                                       Crystalline [Cr.sub.5 (NC.sub.4 H.sub.4).sub.10 (OC.sub.4 H.sub.8).sub.4       ].sup.a                                                                        Atom        Fractional Coordinates                                             Type.sup.b                                                                              10.sup.4 x 10.sup.4 y 10.sup.4 x                                      ______________________________________                                         H.sub.1a -2129      -661       1707                                            H.sub.2a -4154      -55        1219                                            H.sub.3a -3608      1937       -69                                             H.sub.4a -1267      2508       -339                                            H.sub.1b 1053       3405       -617                                            H.sub.2b 3405       4593       -834                                            H.sub.3b 4676       3202       189                                             H.sub.4b 3031       1158       1020                                            H.sub.1c 1013       3445       3687                                            H.sub.2c 364        5592       3881                                            H.sub.3c -1331      5685       2512                                            H.sub.4c -1704      3580       1540                                            H.sub.1d 1881       1460       3743                                            H.sub.2d 3177       -88        3396                                            H.sub.3d 1807       -1790      2120                                            H.sub.4d -291       -1252      1752                                            H.sub.1e -446       -1976      3968                                            H.sub.2e -1997      -4161      4742                                            H.sub.3e -4139      -3699      4803                                            H.sub.4e -3878      -1286      4012                                            H.sub.1fa                                                                               3351       3836       3136                                            H.sub.1fb                                                                               3882       3308       2299                                            H.sub.2fa                                                                               5068       5771       2893                                            H.sub.2fb                                                                               4965       5524       1806                                            H.sub.3fa                                                                               3462       6711       2728                                            H.sub.3fb                                                                               4068       7245       1757                                            H.sub.4fa                                                                               2417       5653       964                                             H.sub.4fb                                                                               1641       5625       1839                                            H.sub.1ga                                                                               -3631      2231       2623                                            H.sub.1gb                                                                               -4455      813        3162                                            H.sub.2ga                                                                               -5037      2381       3901                                            H.sub.2gb                                                                               -3704      3640       3750                                            H.sub.3ga                                                                               -4129      1385       5124                                            H.sub.3gb                                                                               -3307      3025       5266                                            H.sub.4ga                                                                               -2173      1220       5050                                            H.sub.4gb                                                                               -1565      2846       4703                                            ______________________________________                                          .sup.a Hydrogen atoms were included in the structure factor calculations       as idealize/atoms (assuming sp.sup.2 or sp.sup.3hybridization of the           carbon atoms and a C--N bond length of 0.96Å) "riding" on their            respective carbon atoms. The isotropic thermal parameter of each hydrogen      atom was fixed at 1.2 times the equivalent isotropic thermal parameter of      the carbon atoms to which it is covalently bonded                              .sup.b Hydrogen atoms are labeled with the same numerical and literal          subscripts as their carbon atoms with an additional literal subscript (a       or b) where necessary to distinguish between hydrogen atoms bonded to the      same carbon.                                                             

                  TABLE IV                                                         ______________________________________                                         Bond Lengths Involving Nonhydrogen Atoms in                                    Crystalline [Cr.sub.5 (NC.sub.4 H.sub.4).sub.10 (OC.sub.4 H.sub.8).sub.4       ].sup.a                                                                        Type.sup.b                                                                               Length, Å                                                                               Type.sup.b                                                                              Length, Å                                  ______________________________________                                         Cr.sub.1 . . . Cr.sub.2                                                                  3.066(1)     O.sub.1f -C.sub.1f                                                                      1.451(5)                                       Cr.sub.2 . . . Cr.sub.3                                                                  3.121(1)     O.sub.1f -C.sub.4f                                                                      1.453(5)                                                              O.sub.1g -C.sub.1g                                                                      1.448(6)                                       Cr.sub.1 -N.sub.1a                                                                       2.153(3)     O.sub.1g -C.sub.d                                                                       1.451(5)                                       Cr.sub.1 -N.sub.1b                                                                       2.092(3)                                                             Cr.sub.2 -N.sub.1a                                                                       2.178(3)     C.sub.1a -C.sub.2a                                                                      1.360(6)                                       Cr.sub.2 -N.sub.1b                                                                       2.149(3)     C.sub.2a -C.sub.3a                                                                      1.395(6)                                       Cr.sub.2 -N.sub.1c                                                                       2.112(4)     C.sub.3a -C.sub.4a                                                                      1.351(6)                                       Cr.sub.3 -N.sub.1c                                                                       2.172(3)     C.sub.1b -C.sub.2b                                                                      1.338(6)                                       Cr.sub.3 -N.sub.1d                                                                       2.101(4)     C.sub.2b -C.sub.3b                                                                      1.393(7)                                       Cr.sub.3 -N.sub.1e                                                                       2.037(3)     C.sub.3b -C.sub.4b                                                                      1.376(6)                                                              C.sub.1c -C.sub.2c                                                                      1.365(7)                                       Cr.sub.2 -O.sub.1f                                                                       2.082(2)     C.sub.2c -C.sub.3c                                                                      1.400(6)                                       Cr.sub.3 - O.sub.1g                                                                      2.068(3)     C.sub.3c -C.sub.4c                                                                      1.356(6)                                                              C.sub.1d -C.sub.2d                                                                      1.376(7)                                       N.sub.1a -C.sub.1a                                                                       1.399(4)     C.sub.2d -C.sub.3d                                                                      1.396(6)                                       N.sub.1a -C.sub.4a                                                                       1.397(5)     C.sub.3d -C.sub.4d                                                                      1.367(8)                                       N.sub.1b -C.sub.1b                                                                       1.398(5)     C.sub.1e -C.sub.2e                                                                      1.370(5)                                       N.sub.1b -C.sub.4b                                                                       1.379(6)     C.sub.2e -C.sub.3e                                                                      1.374(8)                                       N.sub.1c -C.sub.1c                                                                       1.368(4)     C.sub.3e -C.sub.4e                                                                      1.366(6)                                       N.sub.1c -C.sub.4c                                                                       1.394(6)                                                             N.sub.1d -C.sub.1d                                                                       1.349(5)     C.sub.1f -C.sub.2f                                                                      1.460(6)                                       N.sub.1d -C.sub.4d                                                                       1.377(5)     C.sub.2f -C.sub.3f                                                                      1.474(9)                                       N.sub.1e -C.sub.1e                                                                       1.370(6)     C.sub.3f -C.sub.4f                                                                      1.496(6)                                       N.sub.1e -C.sub.4e                                                                       1.361(6)     C.sub.1g -C.sub.2g                                                                      1.496(8)                                                              C.sub.2g -C.sub.3g                                                                      1.485(7)                                                              C.sub.3g -C.sub.4g                                                                      1.476(9)                                       ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIG. 1.                       

                  TABLE V                                                          ______________________________________                                         Bond Angles Involving Nonhydrogen Atoms in                                     Crystalline [Cr.sub.5 (NC.sub.4 H.sub.4).sub.10 (OC.sub.4 H.sub.8).sub.4       ].sup.a                                                                        Type.sup.b                                                                               Angle, deg  Type.sup.b                                                                               Angle, deg                                     ______________________________________                                         N.sub.1a Cr.sub.1 N.sub.1b                                                                84.8(1)    Cr.sub.1 N.sub.1a Cr.sub.2                                                                90.2(1)                                       N.sub.1a Cr.sub.1 N.sub.1a,.sup.c                                                        .sup. 180.0(-).sup.d                                                                       Cr.sub.1 N.sub.1a C.sub.1a                                                               121.2(2)                                       N.sub.1b Cr.sub.1 N.sub.1a,.sup.c                                                         95.2(1)    Cr.sub.2 N.sub.1a C.sub.1a                                                               118.0(2)                                       N.sub.1b Cr.sub.1 N.sub.1b,.sup.c                                                        .sup. 180.0(-).sup.d                                                                       Cr.sub.1 N.sub.1a C.sub.4a                                                               113.4(2)                                                             Cr.sub.2 N.sub.1a C.sub.4a                                                               110.6(2)                                       N.sub.1a Cr.sub.2 N.sub.1b                                                                82.9(1)    C.sub.1a N.sub.1a C.sub.4a                                                               103.5(3)                                       N.sub.1a Cr.sub.2 N.sub.1c                                                                96.5(1)    Cr.sub.1 N.sub.1b Cr.sub.2                                                                92.6(1)                                       N.sub.1b Cr.sub.2 N.sub.1c                                                               168.9(1)    Cr.sub.1 N.sub.1b C.sub.1b                                                               117.9(2)                                       N.sub.1a Cr.sub.2 O.sub.1f                                                               162.4(1)    Cr.sub.2 N.sub.1b C.sub.1b                                                               107.6(3)                                       N.sub.1b Cr.sub.3 O.sub.1f                                                                89.5(1)    Cr.sub.1 N.sub.1b C.sub. 4b                                                              120.6(3)                                       N.sub.1c Cr.sub.2 O.sub.1f                                                                87.9(1)    Cr.sub.2 N.sub.1b C.sub.4b                                                               113.0(3)                                                             C.sub.1b N.sub.1b C.sub.4b                                                               104.4(3)                                       N.sub.1c Cr.sub.3 N.sub.1d                                                                88.1(1)    Cr.sub.2 N.sub.1c Cr.sub.3                                                                93.5(1)                                       N.sub.1c Cr.sub.3 N.sub.1e                                                               176.5(1)    Cr.sub.2 N.sub.1c C.sub.1c                                                               121.4(3)                                       N.sub.1d Cr.sub.3 N.sub.1e                                                                93.5(1)    Cr.sub.3 N.sub.1c C.sub.1c                                                               100.0(2)                                       N.sub.1c Cr.sub.3 O.sub.1f                                                                88.8(1)    Cr.sub.2 N.sub.1c C.sub.4c                                                               116.1(2)                                       N.sub.1d Cr.sub.3 O.sub.1g                                                               170.4(1)    Cr.sub.3 N.sub.1c C.sub.4c                                                               121.5(2)                                       N.sub.1e Cr.sub.3 O.sub.1g                                                                89.1(1)    C.sub.1c N.sub.1c C.sub.4c                                                               104.2(3)                                                             Cr.sub.3 N.sub.1d C.sub.1d                                                               121.3(3)                                       N.sub.1a C.sub.1a C.sub.2a                                                               110.6(3)    Cr.sub.3 N.sub.1d C.sub.4d                                                               127.8(3)                                       C.sub.1a C.sub.2a C.sub.3a                                                               107.5(4)    C.sub.1d N.sub.1d C.sub.4d                                                               106.4(4)                                       C.sub.2a C.sub.3a C.sub.4a                                                               106.9(4)    Cr.sub.3 N.sub.1e C.sub.1e                                                               126.3(3)                                       C.sub.3a C.sub.4a N.sub.1a                                                               111.5(3)    Cr.sub.3 N.sub.1e C.sub.4e                                                               128.3(3)                                       N.sub.1b C.sub.1b C.sub.2b                                                               111.2(4)    C.sub.1e N.sub.1e C.sub.4e                                                               105.3(3)                                       C.sub.1b C.sub.2b C.sub.3b                                                               107.4(4)                                                             C.sub.2b C.sub.3b C.sub.4b                                                               107.0(4)    Cr.sub.2 O.sub.1f C.sub.1f                                                               131.5(2)                                       C.sub.3b C.sub.4b N.sub.1b                                                               110.1(4)    Cr.sub.2 O.sub.1f C.sub.4f                                                               118.9(2)                                       N.sub.1c C.sub.1c C.sub.2c                                                               110.9(4)    C.sub.1f O.sub.1f C.sub.4f                                                               109.1(3)                                       C.sub.1c C.sub.2c C.sub.3c                                                               106.8(4)    Cr.sub.3 O.sub.1g C.sub.1g                                                               131.9(3)                                       C.sub.2c C.sub.3c C.sub.4c                                                               1072.(4)    Cr.sub.3 O.sub.1g C.sub.4g                                                               118.6(3)                                       C.sub.3c C.sub.4c N.sub.1c                                                               110.9(3)    C.sub.1g O.sub.1g C.sub.4g                                                               109.5(4)                                       N.sub.1d C.sub.1d C.sub.2d                                                               110.3(4)                                                             C.sub.1d C.sub.2d C.sub.3d                                                               106.7(4)    O.sub.1f C.sub.1f C.sub.2f                                                               105.0(4)                                       C.sub.2d C.sub.3d C.sub.4d                                                               106.6(5)    C.sub.1f C.sub.2f C.sub.3f                                                               104.9(4)                                       C.sub.3d C.sub.4d N.sub.1d                                                               109.9(3)    C.sub.2f C.sub.3f C.sub.4f                                                               104.4(4)                                       N.sub.1e C.sub.1e C.sub.2e                                                               110.0(4)    C.sub.3f C.sub.4f O.sub.1f                                                               105.4(4)                                       C.sub.1e C.sub.2e C.sub.3e                                                               107.2(4)    O.sub.1g C.sub.1g C.sub.2g                                                               104.8(4)                                       C.sub.2e C.sub.3e C.sub.4e                                                               106.7(4)    C.sub.1g C.sub.2g C.sub.3g                                                               104.2(5)                                       C.sub.3e C.sub.4e N.sub.1e                                                               110.8(5)    C.sub.2g C.sub.3g C.sub.4g                                                               104.2(4)                                                             C.sub.3g C.sub.4g O.sub.1g                                                               106.1(4)                                       ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIG. 1                              .sup.c Atoms labeled with a prime () are related to nonprimed atoms by th      symmetry operation -x, -y, -z where the fractional coordinates (x, y, z)       are given in Table I.                                                          .sup.d This is a symmetryrequired value and is therefore listed without a      estimated standard deviation.                                            

EXAMPLE V

A single crystal x-ray structure was obtained for Cr(NC₄ H₄)₄, a portion of Product III and shown in FIG. 3. A single crystal x-ray structure was obtained for [Na]₂ [Cr(NC₄ H₄)₄ ].2(OC₄ H₈), Product III and shown in FIG. 4. The description of the single-crystal sample and mounting used for the data collection are as follows:

Color: Red-Orange

Shape: Rectangular parallelepiped

Dimensions: 0.50×0.55×0.65 mm

Crystal Mount: Crystal was glued to the inside of a thin-walled glass capillary and sealed under N₂.

Crystal Orientation: Crystal was oriented with its longest edge nearly parallel to the phi axis of the diffractometer.

Width at Half-height from ω Scans: 0.86°

The space group and cell data are as follows:

Crystal System: Monoclinic

Space Group and Number:² C2/c--C_(2h) ⁶ (no. 15)

Number of Computer-Centered Reflections Used in the Least-Squares Refinement of the Cell Dimensions:

Dimensions: 15 20°>25° C.=20+1°

    ______________________________________                                         Lattice Constants with esd's:                                                  ______________________________________                                         a = 9.552(2)Å                                                                            α = 90.00°                                                                     V = 2697(1)Å.sup.3                              b = 15.118(2)Å                                                                           β = 98.99(1)°                                                                   Z = 4                                               c = 18.967(3)Å                                                                           γ = 90.00°                                                                     λ = 0.71073Å                             ______________________________________                                    

Molecular Weight: 506.52 amu

Calculated Density: 1.248 g/cm⁻³

Linear Absorption Coefficient:^(3a) 0.47 mm⁻¹

Tables VI-X list the resultant parameters used to generate the molecular structures shown in FIGS. 3 and 4.

                  TABLE VI                                                         ______________________________________                                         Atomic Coordinates for Nonhydrogen Atoms in Crystalline                        (Na).sub.2 {Cr(NC.sub.4 H.sub.4).sub.4 }-(2(OC.sub.4 H.sub.8).sup.a                                      Equivalent Isotropic                                 Atom   Fractional Coordinates                                                                            Thermal Parameter,                                   Type.sup.b                                                                            10.sup.4 x                                                                              10.sup.4 y                                                                              10.sup.4 z                                                                            B, Å.sup.2 × 10.sup.c                ______________________________________                                         Anion                                                                          Cr     0.sup.d  2982(1)  2500.sup.d                                                                            58(1)                                          N.sub.1                                                                               1901(4)  2924(2)  3183(2)                                                                               56(1)                                          N.sub.2                                                                               8.sup.d  4343(3)  2500.sup.d                                                                            52(1)                                          N.sub.3                                                                               8.sup.d  1612(3)  2500.sup.d                                                                            70(2)                                          C.sub.11                                                                              3241(5)  2958(3)  3008(3)                                                                               65(2)                                          C.sub.12                                                                              4224(6)  2768(3)  3587(3)                                                                               73(2)                                          C.sub.13                                                                              3513(7)  2638(4)  4146(3)                                                                               82(2)                                          C.sub.14                                                                              2094(7)  2734(4)  3884(3)                                                                               76(2)                                          C.sub.21                                                                               907(5)  4884(3)  2926(3)                                                                               68(1)                                          C.sub.22                                                                               582(4)  5753(3)  2766(3)                                                                               69(2)                                          C.sub.31                                                                               390(5)  1081(3)  1996(4)                                                                               94(2)                                          C.sub.32                                                                               326(7)   213(3)  2189(5)                                                                               133(6)                                         Cation                                                                         Na     2301(2)  6879(1)  1783(1)                                                                               69(1)                                          Solvent of Crystallization                                                     O.sub.1                                                                               2065(4)  5108(2)   838(2)                                                                               83(1)                                          C.sub.41                                                                               2759(11)                                                                               5174(5)    239(4)                                                                              143(4)                                         C.sub.42                                                                               2884(11)                                                                               4319(5)  -79(4) 148(4)                                         C.sub.43                                                                               1893(10)                                                                               3786(5)   264(5)                                                                               142(4)                                         C.sub.44                                                                              1699(9)  4231(4)   902(4)                                                                               120(3)                                         ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIGS. 3 and 4.                      .sup.c This is onethird of the trace of the orthogonalized B.sub.ij            tensor.                                                                        .sup.d This is a symmetryrequired value and is therefore listed without a      estimated standard deviation.                                            

                  TABLE VII                                                        ______________________________________                                         Anisotropic Thermal Parameters for Nonhydrogen atoms in                        Crystalline {Na}.sub.2 {Cr(NC.sub.4 H.sub.4).sub.4 }-2 OC.sub.4 H.sub.8.su     p.a,b                                                                          Atom  Anisotropic Thermal Parameter (Å.sup.2 × 10)                   Type.sup.c                                                                           B.sub.11                                                                               B.sub.22                                                                               B.sub.33                                                                             B.sub.12                                                                              B.sub.13                                                                              B.sub.23                             ______________________________________                                         Anion                                                                          Cr    64(1)   34(1)   55(1) 0.sup.d                                                                               15(1)  0.sup.d                              N.sub.1                                                                              69(2)   44(2)   56(2)  6(1)  12(1)    6(1)                               N.sub.2                                                                              64(3)   39(2)   56(3) 0.sup.d                                                                               16(2)  0.sup.d                              N.sub.3                                                                              65(3)   38(2)   107(4)                                                                               0.sup.d                                                                               14(3)  0.sup.d                              C.sub.11                                                                             78(3)   50(2)   70(3) -6(2)  18(2)    2(2)                               C.sub.12                                                                             70(3)   62(3)   84(3)  4(2)   7(2)   -8(2)                               C.sub.13                                                                             103(4)  79(3)   58(3)  22(3) -8(3)   0(2)                                C.sub.14                                                                             86(3)   86(3)   58(3)  16(3) 16(2)   5(2)                                C.sub.21                                                                             66(2)   45(2)   70(3) -2(2)  15(2)   -6(2)                               C.sub.22                                                                             68(3)   38(2)   105(4)                                                                               -7(2)  27(2)   -9(2)                               C.sub.31                                                                             65(3)   61(3)   152(5)                                                                                6(2)   9(3)  -36(3)                               C.sub. 32                                                                            71(5)   46(2)   266(15)                                                                               6(3)  -20(6) -44(4)                               Cation                                                                         Na    70(1)   57(1)   81(1) -2(1)  15(1)  -15(1)                               Solvent of Crystallaization                                                    O.sub.1                                                                              108(2)  65(2)   82(2) -10(2) 38(2)  -16(2)                               C.sub.41                                                                             222(8)  112(5)  116(5)                                                                               -46(5) 92(6)  -22(4)                               C.sub.42                                                                             192(8)  168(8)  107(5)                                                                                12(6) 70(5)  -32(5)                               C.sub.43                                                                             174(6)  109(6)  177(8)                                                                               -27(5) 48(6)  -69(6)                               C.sub.44                                                                             177(6)  77(4)   124(5)                                                                               -21(4) 76(5)  -14(3)                               ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b The form of the anisotropic thermal parameter is given in referenc      8 on page 6 of the structure report.                                           .sup.c Atoms are labeled in agreement with FIGS. 3 and 4.                      .sup.d This is a symmetryrequired value and is therefore listed without a      estimated standard deviation.                                            

                  TABLE VIII                                                       ______________________________________                                         Atomic Coordinates for Hydrogen Atoms in                                       Crystalline {Na}.sub.2 {Cr( .sub.4 H.sub.4).sub.4 }-2(OC.sub.4 H.sub.8).su     p.a                                                                            Atom         Fractional Coordinates                                            Type.sup.b                                                                               10.sup.4 x   10.sup.4 y                                                                             10.sup.4 z                                      ______________________________________                                         Anion                                                                          H.sub.11  3456         3881    2541                                            H.sub.12  5235         2748    3680                                            H.sub.13  3922         2488    4628                                            H.sub.14  1341         2679    4164                                            H.sub.21  1665         4687    3285                                            H.sub.22  1071         6262    2985                                            H.sub.31   706         1274    1565                                            H.sub.32   483         -301    1937                                            Solvent of Crystallization                                                     H.sub.41a 2250         5576    -100                                            H.sub.41b 3710         5388     385                                            H.sub.42a 3756         4891     -1                                             H.sub.42b 2464         4348    -583                                            H.sub.43a  995         3707    -39                                             H.sub.43b 2326         3220     377                                            H.sub.44a 2295         3973    1304                                            H.sub.44b  723         4191     969                                            ______________________________________                                          .sup.a Hydrogen atoms were included in the structure factor calculations       as idealized atoms (assuming sp.sup.2 or sp.sup.3hybridization of the          carbon atoms and a C--H bond length of 0.96Å) "riding" on their            respective carbon atoms. The isotropic thermal parameter of each hydrogen      atom was fixed at 1.2 times the equivalent isotropic thermal parameter of      the carbon atom to which it is covalently bonded.                              .sup.b Hydrogen atoms are labeled with the same numerical subscripts as        the carbon atoms to which they are covalently bonded with an additional        literal subscript (a or b) where necessary to distinguish between              hydrogens bonded to the same carbon.                                     

                  TABLE IX                                                         ______________________________________                                         Anion Bond lengths and Bond Angles                                             Involving Nonhydrogen atoms in Crystalline                                     ({Na}.sub.2 {Cr(NC.sub.4 H.sub.4).sub.4 }-2(OC.sub.4 H.sub.8).sup.a            ______________________________________                                         Type.sup.b                                                                               Length, Å                                                                              Type.sup.b                                                                               Length, Å                                  ______________________________________                                         Cr--N.sub.1                                                                              2.057(3)    C.sub.11 --C.sub.12                                                                      1.355(7)                                       Cr--N.sub.2                                                                              2.056(4)    C.sub.12 --C.sub.13                                                                      1.361(9)                                       Cr--N.sub.3                                                                              2.072(5)    C.sub.13 --C.sub.14                                                                      1.374(9)                                                             C.sub.21 --C.sub.22                                                                      1.372(6)                                       N.sub.1 --C.sub.11                                                                       1.369(7)    C.sub.22 --C.sub.22,.sup.c                                                               1.379(9)                                       N.sub.1 --C.sub.14                                                                       1.344(6)    C.sub.31 --C.sub.32                                                                      1.376(7)                                       N.sub.2 --C.sub.21                                                                       1.360(5)    C.sub.32 --C.sub.32,.sup.c                                                                1.327(18)                                     N.sub.3 --C.sub.31                                                                       1.344(7)                                                             ______________________________________                                         Type.sup.b                                                                               Angle, deg. Type.sup.b                                                                               Angle, deg.                                    ______________________________________                                         N.sub.1 CrN.sub.2                                                                         92.5(1)    N.sub.1 C.sub.11 C.sub.12                                                                110.5(5)                                       N.sub.1 CrN.sub.3                                                                         87.5(1)    C.sub.11 C.sub.12 C.sub.13                                                               107.3(5)                                       N.sub.1 CrN.sub.1,.sup.c                                                                 175.1(2)    C.sub.12 C.sub.13 C.sub.14                                                               106.4(5)                                       N.sub.2 CrN.sub.3                                                                         180.0(-).sup.d                                                                            N.sub.1 C.sub.14 C.sub.13                                                                110.9(5)                                                             N.sub.2 C.sub.21 C.sub.22                                                                110.2(4)                                       CrN.sub.1 C.sub.11                                                                       127.5(5)    C.sub.21 C.sub.22 C.sub.22,.sup.c                                                        106.8(3)                                       CrN.sub.1 C.sub.14                                                                       127.1(4)    N.sub.3 C.sub.31 C.sub.32                                                                109.1(6)                                       C.sub.11 N.sub.1 C.sub.14                                                                104.9(4)    C.sub.31 C.sub.32 C.sub.32,.sup.c                                                        107.5(5)                                       CrN.sub.2 C.sub.21                                                                       127.0(2)                                                             C.sub.21 N.sub.2 C.sub.21,.sup.c                                                         106.0(5)                                                             CrN.sub.3 C.sub.31                                                                       126.7(3)                                                             C.sub.31 N.sub.3 C.sub.31,.sup.c                                                         106.7(6)                                                             ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIG. 4.                             .sup.c Atoms labeled with a prime(') are related to nonprimed atoms by th      symmetry operation x, y z.                                               

                  TABLE X                                                          ______________________________________                                         Bond Lengths and Angles Involving the                                          Nonhydrogen Atoms of the Cation and                                            Solvent of Crystallization in                                                  {Na}.sub.2 {Cr(NC.sub.4 H.sub.4).sub.4 }-2(OC.sub.4 H.sub.8).sup.a             ______________________________________                                         Type.sup.b Length, Å                                                                              Type.sup.b                                                                               Length, Å                                 ______________________________________                                         Na--O.sub.1                                                                               2.313(4)    O.sub.1 --C.sub.41                                                                        1.390(10)                                                           O.sub.1 --C.sub.44                                                                        1.382(7)                                     Na . . .N.sub.1".sup.c                                                                    2.888(4)                                                            Na . . . N.sub.3".sup.c                                                                   2.830(4)    C.sub.41 --C.sub.42                                                                      1.43(1)                                                              C.sub.42 --C.sub.43                                                                      1.42(1)                                                              C.sub.43 --C.sub.44                                                                      1.42(1)                                       ______________________________________                                         Type.sup.b Angle, deg. Type.sup.b                                                                               Angle, deg.                                   ______________________________________                                         O.sub.1 NaN.sub.1".sup.c                                                                  128.6(3)    C.sub.41 O.sub.1 C.sub.44                                                                107.9(5)                                      O.sub.1 NaN.sub.3".sup.c                                                                  121.8(3)                                                            N.sub.1" NaN.sub.3".sup.c                                                                  59.9(3)    O.sub.1 C.sub.41 C.sub.42                                                                109.0(7)                                                             C.sub.41 C.sub.42 C.sub.43                                                               105.0(8)                                      NaO.sub.1 C.sub.41                                                                        125.7(4)    C.sub.42 C.sub.43 C.sub.44                                                               107.0(7)                                      NaO.sub.1 C.sub.44                                                                        121.8(4)    O.sub.1 C.sub.44 C.sub.43                                                                107.6(7)                                      ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIG. 4.                             .sup.c Atoms labeled with a double prime(") are related to nonprimed atom      by the symmetry operations x, y, z.                                      

EXAMPLE VI

Single crystal x-ray structures were obtained for [Cr(NC₄ H₄)₅ (OC₄ H₈)], shown in FIG. 5, and [Cr(NC₄ H₄)₅ (OC₄ H₈)][Na]₂.4(OC₄ H₈), Product IV, and shown in FIG. 6. The description of the single-crystal sample and mounting used for data collection are as follows:

Color: Purple

Shape: Rectangular parallelepiped

Dimensions: 0.50×0.55×0.63 mm

Crystal Mount: Crystal was glued to the inside of a thin-walled glass capillary and sealed under N₂.

Crystal Orientation: Crystal was oriented with its longest edge nearly parallel to the phi axis of the diffractometer.

Width at Half-height from ω Scans: 0.42°

The space group and cell data are as follows:

Crystal System: Monoclinic

Space Group and Number:² P2₁ --C₂ ² (No. 4)

Number of Computer-Centered Reflections Used in the Least-Squares Refinement of the Cell Dimensions:

15 20°>20° °C.=20°±1°

    ______________________________________                                         Lattice Constants with esd's:                                                  ______________________________________                                         a = 10.042(2)Å                                                                           α = 90.00°                                                                      V = 2162(1)Å.sup.3                             b = 17.242(4)Å                                                                           β = 106.54(2)°                                                                   Z = 2                                              c = 13.025(3)Å                                                                           γ = 90.00°                                                                      λ = 0.71073Å                            ______________________________________                                    

Molecular Weight=788.93 amu

Calculated Density: 1.212 g/cn⁻³

Linear Absorption Coefficient:^(3a) 0.32 mm⁻¹

Tables XI-XV list the resultant parameters used to generate the molecular structures shown in FIGS. 5 and 6.

                  TABLE XI                                                         ______________________________________                                         Atomic Coordinates for Nonhydrogen Atoms in                                    Crystalline [Cr(NC.sub.4 N.sub.4).sub.5 (OC.sub.4 N.sub.8)][Na].sub.2          -4(OC.sub.4 H.sub.8).sup.a                                                                                Equivalent                                                                     Isotropic Thermal                                   Atom  Fractional Coordinates                                                                              Parameter                                           Type.sup.b                                                                           10.sup.4 x                                                                               10.sup.4 y                                                                              10.sup.4 z                                                                             B, Å.sup.2 × 10.sup.c               ______________________________________                                         Anion                                                                          Cr     198(1)   1477     2531(10)                                                                               32(1)                                         N.sub.1a                                                                             1694(5)   2026(3)  2028(4) 40(2)                                         C.sub.1a                                                                             1749(7)   2782(4)  1742(6) 48(2)                                         C.sub.2a                                                                             2929(8)   2926(5)  1420(7) 66(3)                                         C.sub.3a                                                                             3661(7)   2236(5)  1554(6) 62(3)                                         C.sub.4a                                                                             2899(6)   1695(5)  1913(5) 52(2)                                         N.sub.1b                                                                             1651(5)   1087(3)  3885(4) 40(2)                                         C.sub.1b                                                                             1463(8)    560(4)  4575(5) 48(2)                                         C.sub.2b                                                                             2572(9)    518(6)  5423(8) 82(4)                                         C.sub.3b                                                                             3554(8)   1064(6)  5275(6) 70(3)                                         C.sub.4b                                                                             2952(6)   1382(5)  4340(5) 48(2)                                         N.sub.1c                                                                             -1326(5)  1888(3)  1250(4) 38(2)                                         C.sub.1c                                                                             -1200(8)  2172(4)   266(6) 51(2)                                         C.sub.2c                                                                             -2458(8)  2270(5)  -476(6) 58(3)                                         C.sub.3c                                                                             -3435(8)  2038(6)   56(7)  75(3)                                         C.sub.4c                                                                             -2710(7)  1826(5)  1091(6) 56(3)                                         N.sub.1d                                                                             - 32(5)   2455(4)  3445(5) 43(2)                                         C.sub.1d                                                                              504(7)   2562(5)  4505(6) 49(2)                                         C.sub.2d                                                                              107(9)   3278(5)  4774(8) 72(3)                                         C.sub.3d                                                                             -698(8)   3629(5)  3832(6) 59(3)                                         C.sub.4d                                                                             -769(7)   3108(4)  3055(6) 52(2)                                         N.sub.1e                                                                              315(5)    505(4)  1690(4) 40(2)                                         C.sub.1e                                                                             -574(8)    277(5)   704(6) 55(3)                                         C.sub.2e                                                                             -197(10)  -432(5)   403(7) 67(3)                                         C.sub.3e                                                                              990(10)  -662(6)  1256(8) 79(4)                                         C.sub.4e                                                                             1265(8)   -92(4)   2016(7) 51(3)                                         O.sub.1f                                                                             -1356(4)   926(3)  3083(4) 43(1)                                         C.sub.1f                                                                             -2047(7)  1244(5)  3800(6) 57(3)                                         C.sub.2f                                                                             -3263(10)  713(6)  3706(9) 98(5)                                         C.sub.3f                                                                             -2833(11) -21(6)   3402(8) 93(4)                                         C.sub.4f                                                                             -1930(8)   171(5)  2724(7) 64(3)                                         Cation 1                                                                       Na.sub.1                                                                             2254(3)   3336(2)  3737(3) 75(1)                                         Cation 2                                                                       Na.sub.2                                                                             1430(3)    974(2)   126(2) 62(1)                                         Solvent Molecules of Crystallization                                           O.sub.1g                                                                             4576(6)   3329(4)  4706(5) 83(2)                                         C.sub.1g                                                                             5748(9)    3100(10)                                                                               4433(9) 125(6)                                        C.sub.2g                                                                              6723(12)  2831(11)                                                                               5281(9) 145(7)                                        C.sub.3g                                                                              6503(15)  3272(11)                                                                                6146(11)                                                                              204(8)                                        C.sub.4g                                                                              5037(14)  3498(11)                                                                                5737(10)                                                                              170(8)                                        O.sub.1h                                                                             2342(7)   4602(4)  3279(6) 97(3)                                         C.sub.1h                                                                              1316(11) 5151(7)   2894(10)                                                                              112(5)                                        C.sub.2h                                                                              2017(16) 5830(9)   2541(11)                                                                              153(7)                                        C.sub.3h                                                                              3180(12)  5561(10)                                                                                2425(10)                                                                              131(6)                                        C.sub.4h                                                                              3551(13) 4848(7)   3070(11)                                                                              115(6)                                        O.sub.1i                                                                             1391(7)   1752(4)  -1377(4)                                                                               80(2)                                         C.sub.1i                                                                              2235(19)  1594(11)                                                                               -1998(13)                                                                              160(8)                                        C.sub.2i                                                                              2716(17)  2287(14)                                                                               -2337(15)                                                                              165(10)                                       C.sub.3i                                                                              1991(28)  2906(11)                                                                               -1934(14)                                                                              204(12)                                       C.sub.4i                                                                              1010(16) 2533(7)  -1523(9)                                                                               128(6)                                        O.sub.ij                                                                             3037(5)    155(4)  -264(5) 72(2)                                         C.sub.1j                                                                              4389(10)  48(7)    427(9) 113(5)                                        C.sub.2j                                                                              4998(16) -571(10)  -23(16)                                                                               174(8)                                        C.sub.3j                                                                              4001(11) -840(8)  -1006(10)                                                                              127(6)                                        C.sub.4j                                                                              2728(11) -493(7)  -974(8) 92(4)                                         ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIGS. 5 and 6.                      .sup.c This is onethird of the trace of the orthogonalized B.sub.ij            tensor.                                                                  

                  TABLE XII                                                        ______________________________________                                         Anisotropic Thermal Parameters for Nonhydrogen                                 Atoms in Crystalline [Cr(NC.sub.4 H.sub.4).sub.5 (OC.sub.4 H.sub.8)][Na].s     ub.2 -                                                                         4(OC.sub.4 H.sub.8).sup.a                                                            Anisotropic Thermal Parameter (Å.sup.2 × 10)                   Type.sup.c                                                                           B.sub.11 B.sub.22                                                                               B.sub.33                                                                             B.sub.12                                                                              B.sub.13                                                                             B.sub.23                             ______________________________________                                         Anion                                                                          Cr     29(1)    31(1)   38(1)                                                                                 1(1)  12(1)                                                                                 1(1)                               N.sub.1a                                                                              33(2)    44(3)   44(3)                                                                                -1(2)  11(2)                                                                                 5(2)                               C.sub.1a                                                                              48(4)    37(3)   59(4)                                                                                -0(3)  15(3)                                                                                 3(3)                               C.sub.2a                                                                              55(4)    61(5)   90(5)                                                                               -19(4)  34(4)                                                                                 13(4)                              C.sub.3a                                                                              37(3)    82(6)   76(5)                                                                                -9(3)  33(3)                                                                                 2(4)                               C.sub.4a                                                                              40(3)    64(5)   52(4)                                                                                 4(3)  16(3)                                                                                -5(3)                               N.sub.1b                                                                              36(2)    44(3)   36(3)                                                                                 7(2)   5(2)                                                                                 12(2)                              C.sub.1b                                                                              52(4)    51(4)    40(3)                                                                               -2(3)   9(3)                                                                                 10(3)                              C.sub.2b                                                                              73(5)    85(6)   83(6)                                                                                 2(5)  13(4)                                                                                 44(5)                              C.sub.3b                                                                              51(4)    88(6)   54(4)                                                                                 0(4) -13(3)                                                                                 12(4)                              C.sub.4b                                                                              41(3)    55(4)   45(3)                                                                                 0(3)   5(2)                                                                                 4(4)                               N.sub.1c                                                                              33(2)    41(3)   39(3)                                                                                 4(2)   9(2)                                                                                 1(2)                               C.sub.1c                                                                              52(4)    51(4)   51(4)                                                                                 6(3)  16(3)                                                                                 5(3)                               C.sub.2c                                                                              64(5)    62(5)   37(4)                                                                                -1(4)  -4(3)                                                                                 4(4)                               C.sub.3c                                                                              32(3)    92(6)   89(6)                                                                                 4(4)  -3(4)                                                                                 29(5)                              C.sub.4c                                                                              42(3)    78(5)   48(4)                                                                                -1(3)   9(3)                                                                                 14(4)                              N.sub.1d                                                                              31(2)    44(3)   56(3)                                                                                 4(2)  13(2)                                                                                -1(3)                               C.sub.1d                                                                              44(3)    60(5)   39(4)                                                                                -5(3)   8(3)                                                                                -11(3)                              C.sub.2d                                                                              63(4)    70(6)   84(6)                                                                               -11(4)  20(4)                                                                                -47(5)                              C.sub.3d                                                                              69(4)    43(4)   73(5)                                                                                  9(3)                                                                                32(4)                                                                                -14(4)                              C.sub.4d                                                                              42(3)    53(4)   63(4)                                                                                 8(3)  17(3)                                                                                 3(4)                               N.sub.1e                                                                              47(3)    36(3)   39(3)                                                                                -3(2)  17(2)                                                                                -7(2)                               C.sub.1e                                                                              59(4)    49(4)   53(4)                                                                               -15(3)  11(3)                                                                                -1(4)                               C.sub.2e                                                                              92(5)    48(4)   69(5)                                                                               -20(4)  36(4)                                                                                -26(4)                              C.sub.3e                                                                              91(6)    45(5)  106(7)                                                                                 4(4)  37(5)                                                                                -13(5)                              C.sub.4e                                                                              62(4)    23(3)   69(5)                                                                                 7(3)  20(4)                                                                                -7(3)                               O.sub.1f                                                                              40(2)    42(2)   51(2)                                                                                -4(2)  20(2)                                                                                 2(2)                               C.sub.1f                                                                              61(4)    64(5)   60(4)                                                                                -2(3)  39(3)                                                                                 4(4)                               C.sub.2f                                                                              81(6)    95(7)  144(8)                                                                               -24(5)  74(6)                                                                                 1(6)                               C.sub.3f                                                                             109(7)    80(6)  177(7)                                                                               -26(5)  75(6)                                                                                -3(6)                               C.sub.4f                                                                              61(4)    53(4)   85(5)                                                                               -27(4)  30(4)                                                                                -16(4)                              Cation 1                                                                       Na.sub.1                                                                              57(2)    71(2)   95(2)                                                                                -13(1)                                                                                21(2)                                                                                - 2(2)                              Cation 2                                                                       Na.sub.2                                                                              68(2)    69(2)   56(2)                                                                                -2(1)  30(1)                                                                                -3(2)                               Solvent Molecules of Crystallization                                           O.sub.1g                                                                              58(3)    95(4)   92(4)                                                                                -8(3)  15(3)                                                                                -2(4)                               C.sub.1g                                                                              54(5)   215(14) 108(8)                                                                                 0(7)  29(5)                                                                                -7(9)                               C.sub.2g                                                                              96(7)   226(15) 121(9)                                                                                52(9)  43(7)                                                                                 51(10)                             C.sub.3g                                                                             129(10   277(19) 148(11)                                                                               52(12)                                                                               -56(9)                                                                               -134(13)                             C.sub.4g                                                                             134(10)  250(18) 128(10)                                                                               44(11)                                                                                39(9)                                                                                -89(11)                             O.sub.1h                                                                              71(4)    68(4)  152(6)                                                                                -8(3)  32(4)                                                                                -3(4)                               C.sub.1h                                                                              92(7)    95(8)  144(9)                                                                                -2(6)  28(7)                                                                                -3(7)                               C.sub.2h                                                                             212(14)  108(9)  140(10)                                                                               36(10)                                                                                50(10)                                                                                66(9)                              C.sub.3h                                                                              99(8)   175(14) 101(8)                                                                                -6(9)  -2(6)                                                                                 32(9)                              C.sub.4h                                                                              99(8)    79(7)  168(11)                                                                              -13(6)  38(8)                                                                                 29(8)                              O.sub.1i                                                                              98(4)    82(4)   73(3)                                                                                 8(3)  47(3)                                                                                 13(3)                              C.sub.1i                                                                             230(15)  128(11) 168(12)                                                                                 8(11)                                                                               131(12)                                                                               74(10)                             C.sub.2i                                                                             112(10)  222(21) 156(15)                                                                                1(12)                                                                                28(10)                                                                                23(16)                             C.sub.3i                                                                             370(26)  124(12) 135(12)                                                                              -93(15)                                                                                99(15)                                                                                34(10)                             C.sub.4i                                                                             223(13)   81(7)  106(8)                                                                                32(8)  91(9)                                                                                 31(6)                              O.sub.1j                                                                              59(3)    64(3)   94(4)                                                                                 5(3)  22(3)                                                                                -21(3)                              C.sub.1j                                                                              88(7)   101(8)  133(9)                                                                                19(6)   2(6)                                                                                -58(7)                              C.sub.2j                                                                              94(8)   190(14) 205(13)                                                                               73(10)                                                                               -11(9)                                                                                -90(13)                             C.sub.3j                                                                              83(7)   130(10) 160(10)                                                                               16(7)  20(7)                                                                                -86(9)                              C.sub.4j                                                                              82(6)   104(8)   92(7)                                                                                -7(6)  29(5)                                                                                -41(6)                              ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b The form of the anisotropic thermal parameter is given in referenc      8 on page 6 of the structure report.                                           .sup.c Atoms are labeled in agreement with FIGS. 5 and 6.                

                  TABLE XIII                                                       ______________________________________                                         Atomic Coordinates for Hydrogen Atoms in                                       Crystalline [Cr(NC.sub.4 H.sub.4).sub.5 (OC.sub.4 H.sub.8)][Na].sub.2 -        4(OC.sub.4 H.sub.8).sup.a                                                      Atom     Fractional Coordinates                                                Type.sup.b                                                                              10.sup.4 x 10.sup.4 y 10.sup.4 z                                      ______________________________________                                                Anion                                                                   H.sub.1a 1061       3165       1756                                            H.sub.2a 3182       3406       1151                                            H.sub.3a 4547       2153       1428                                            H.sub.4a 3162       1162       2059                                            H.sub.1b 637        254        4479                                            H.sub.2b 2692       174        6022                                            H.sub.3b 4453       1179       5753                                            H.sub.4b 3373       1775       4016                                            H.sub.1c -326       2281       132                                             H.sub.2c -2637      2453       -1199                                           H.sub.3c -4426      2031       -243                                            H.sub.4c -3137      1655       1623                                            H.sub.1d 1070       2197       4997                                            H.sub.2d 349        3499       5480                                            H.sub.3d -1115      4135       3762                                            H.sub.4d -1278      3184       2317                                            H.sub.1e -1346      578        293                                             H.sub.2e -630       -712       -243                                            H.sub.3e 1503       -1135      1285                                            H.sub.4e 1999       -107       2676                                            H.sub.1fa                                                                               -1447      1250       4520                                            H.sub.1fb                                                                               -2359      1762       3588                                            H.sub. 2fa                                                                              -4069      899        3170                                            H.sub.2fb                                                                               -3468      674        4380                                            H.sub.3fa                                                                               -2341      -312       4022                                            H.sub.3fb                                                                               -3620      -314       2996                                            H.sub.4fa                                                                               -2417      184        1980                                            H.sub.4fb                                                                               -1165      -201       2831                                                   Solvent of Crystallization                                              H.sub.1ga                                                                               6103       3536       4135                                            H.sub.1gb                                                                               5503       2694       3909                                            H.sub.2ga                                                                               6629       2283       5371                                            H.sub.2gb                                                                               7629       2940       5209                                            H.sub.3ga                                                                               6644       2947       6766                                            H.sub.3gb                                                                               7102       3717       6322                                            H.sub.4ga                                                                               4960       4045       5839                                            H.sub.4gb                                                                               4493       3223       6118                                            H.sub.1ha                                                                               596        4950       2301                                            H.sub.1hb                                                                               921        5310       3451                                            H.sub.2ha                                                                               2205       6231       3073                                            H.sub.2hb                                                                               1449       6034       1874                                            H.sub.3ha                                                                               3066       5447       1684                                            H.sub.3hb                                                                               3908       5936       2669                                            H.sub.4ha                                                                               4260       4953       3725                                            H.sub.4hb                                                                               3874       4459       2671                                            H.sub.1ia                                                                               3007       1289       -1594                                           H.sub.1ib                                                                               1721       1306       -2615                                           H.sub.2ia                                                                               3703       2328       -2031                                           H.sub.2ib                                                                               2496       2303       -3103                                           H.sub.3ia                                                                               1541       3249       -2509                                           H.sub.3ib                                                                               2638       3195       -1381                                           H.sub.4ia                                                                               101        2580       -2020                                           H.sub.4ib                                                                               1010       2761       -851                                            H.sub.1ja                                                                               4929       513        470                                             H.sub.1jb                                                                               4341       -91        1129                                            H.sub.2ja                                                                               5823       -388       -178                                            H.sub.2jb                                                                               5232       - 992      479                                             H.sub.3ja                                                                               3930       -1396      -1018                                           H.sub.3jb                                                                               4261       -668       -1623                                           H.sub.4ja                                                                               2185       -862       -715                                            H.sub.4jb                                                                               2215       -324       -1678                                           ______________________________________                                          .sup.a Hydrogen atoms were included in the structure factor calculations       as idealized atoms (assuming sp.sup.2-  or sp.sup.3-  hybridization of th      carbon atoms and a C--H bond length of 0.96Å) "riding" on their            respective carbon atoms. The isotropic thermal parameter of each hydrogen      atom was fixed at 1.2 times the equivalent isotropic thermal parameter of      the carbon atom to which it is covalently bonded.                              .sup.b Hydrogen atoms are labeled with the same numerical and literal          subscripts as their carbon atoms with an additional literal subscript (a,      or b) where necessary to distinguish between hydrogen atoms bonded to the      same carbon.                                                             

                  TABLE XIV                                                        ______________________________________                                         Bond Lengths Involving Nonhydrogen Atoms in                                    Crystalline [Cr(NC.sub.4 N.sub.4).sub.5 (OC.sub.4 H.sub.8)][Na].sub.2          -4(OC.sub.4 H.sub.8).sup.a                                                     Type b     Length, Å                                                                              Type b    Length, Å                                 ______________________________________                                         Cr--N.sub.1a                                                                              2.035 (6)   Na.sub.1 --O.sub.1g                                                                      2.314 (6)                                     Cr--N.sub.1b                                                                              2.056 (5)  Na.sub.1 --O.sub.1h                                                                       2.271 (8)                                     Cr--N.sub.1c                                                                              2.044 (5)                                                           Cr--N.sub.1d                                                                              2.114 (6)  Na.sub.2 --O.sub.1i                                                                       2.365 (7)                                     Cr--N.sub.1e                                                                              2.024 (6)  Na.sub.2 --O.sub.1j                                                                       2.307 (7)                                     Cr--O.sub.1f                                                                              2.120 (5)  C.sub.1g --C.sub.2g                                                                       1.33 (2)                                                            C.sub.2g --C.sub.3g                                                                       1.43 (2)                                      N.sub.1a --C.sub.1a                                                                       1.36 (1)   C.sub.3g --C.sub.4g                                                                       1.47 (2)                                      N.sub.1a --C.sub.4a                                                                       1.38 (1)   C.sub.1h --C.sub.2h                                                                       1.51 (2)                                      N.sub.1b --C.sub.1b                                                                       1.33 (1)   C.sub.2h --C.sub.3h                                                                       1.30 (2)                                      N.sub.1b --C.sub.4b                                                                       1.37 (1)   C.sub.3h --C.sub.4h                                                                       1.48 (2)                                      N.sub.1c --C.sub.1c                                                                       1.41 (1)   C.sub.1i --C.sub.2i                                                                       1.41 (3)                                      N.sub.1c --C.sub.4c                                                                       1.35 (1)   C.sub.2i --C.sub.3i                                                                       1.47 (3)                                      N.sub.1d --C.sub.1d                                                                       1.34 (1)   C.sub.3i --C.sub.4i                                                                       1.40 (3)                                      N.sub.1d --C.sub.4d                                                                       1.36 (1)   C.sub.1j --C.sub.2j                                                                       1.44 (2)                                      N.sub.1e --C.sub.1e                                                                       1.40 (1)   C.sub.2j --C.sub.3j                                                                       1.46 (2)                                      N.sub.1e --C.sub.4e                                                                       1.39 (1)   C.sub.3j --C.sub.4j                                                                       1.42 (2)                                      O.sub.1f --C.sub.1f                                                                       1.42 (1)   O.sub.1g --C.sub.1g                                                                       1.38 (1)                                      O.sub.1f --C.sub.4f                                                                       1.44 (1)   O.sub.1g --C.sub.4g                                                                       1.32 (1)                                                            O.sub.1h --C.sub.1h                                                                       1.38 (1)                                      C.sub.1a --C.sub.2a                                                                       1.39 (1)   O.sub.1h --C.sub.4h                                                                       1.39 (2)                                      C.sub.2a --C.sub.3a                                                                       1.38 (1)   O.sub.1i --C.sub.1i                                                                       1.36 (2)                                      C.sub.3a --C.sub.4a                                                                       1.37 (1)   O.sub.1i --C.sub.4i                                                                       1.40 (1)                                      C.sub.1b --C.sub.2b                                                                       1.33 (1)   O.sub.1j --C.sub.1j                                                                       1.41 (1)                                      C.sub.2b --C.sub.3b                                                                       1.42 (1)   O.sub.1j --C.sub.4j                                                                       1.43 (1)                                      C.sub.3b --C.sub.4b                                                                       1.31 (1)                                                            C.sub.1c --C.sub.2c                                                                       1.37 (1)   Na.sub.1 --C.sub.1a                                                                       2.678 (8)                                     C.sub.2c --C.sub.3c                                                                       1.41 (1)   Na.sub.1 --N.sub.1d                                                                       2.688 (7)                                     C.sub.3c --C.sub.4c                                                                       1.39 (1)   Na.sub.1 --C.sub.1d                                                                       2.621 (9)                                     C.sub.1d --C.sub.2d                                                                       1.37 (1)                                                            C.sub.2d --C.sub.3d                                                                       1.40 (1)                                                            C.sub.3d --C.sub.4d                                                                       1.34 (1)   Na.sub.2 --C.sub.4a                                                                       2.681 (7)                                     C.sub.1e --C.sub.2e                                                                       1.37 (1)   Na.sub.2 --C.sub.1e                                                                       2.630 (9)                                     C.sub.2e --C.sub.3e                                                                       1.43 (1)                                                            C.sub.3e --C.sub.4e                                                                       1.37 (1)                                                            C.sub.1f --C.sub.2f                                                                       1.50 (1)                                                            C.sub.2f --C.sub.3f                                                                       1.43 (2)                                                            C.sub.3f --C.sub.4f                                                                       1.49 (2)                                                            ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIG. 6.                       

                  TABLE XV                                                         ______________________________________                                         Bond Angles Involving Nonhydrogen Atoms in                                     Crystalline [Cr(NC.sub.4 H.sub.4).sub.5 (OC.sub.4 H.sub.8)][Na].sub.2          -4(OC.sub.4 H.sub.8).sup.a                                                     Type.sup.b                                                                               Angle, deg  Type.sup.b                                                                               Angle, deg                                     ______________________________________                                         N.sub.1a CrN.sub.1b                                                                      91.2 (2)    O.sub.1g Na.sub.1 O.sub.1h                                                               92.3 (3)                                       N.sub.1a CrN.sub.1c                                                                      91.4 (2)    O.sub.1g Na.sub.1 C.sub.1a                                                               114.3 (3)                                      N.sub.1a CrN.sub.1d                                                                      91.1 (2)    O.sub.1g Na.sub.1 N.sub.1d                                                               139.6 (3)                                      N.sub.1a CrN.sub.1e                                                                      92.8 (2)    O.sub.1g Na.sub.1 C.sub.1d                                                               118.0 (3)                                      N.sub.1a CrO.sub.1f                                                                      178.7 (2)   O.sub.1h Na.sub.1 C.sub.1a                                                               95.6 (3)                                       N.sub.1b CrN.sub.1c                                                                      176.2 (2)   O.sub.1h Na.sub.1 N.sub.1d                                                               127.0 (2)                                      N.sub.1b CrN.sub.1d                                                                      86.7 (2)    O.sub.1h Na.sub.1 C.sub.1d                                                               132.1 (3)                                      N.sub.1b CrN.sub.1e                                                                      93.3 (2)    C.sub.1a Na.sub.1 N.sub.1d                                                               75.1 (2)                                       N.sub.1b CrO.sub.1f                                                                      88.5 (2)    C.sub.1a Na.sub.1 C.sub.1d                                                               103.1 (3)                                      N.sub.1c CrN.sub.1d                                                                      90.4 (2)    N.sub.1d Na.sub.1 C.sub.1d                                                               29.3 (2)                                       N.sub.1c CrN.sub.1e                                                                      89.4 (2)                                                             N.sub. 1c CrO.sub.1f                                                                     88.8 (2)    O.sub.1i Na.sub.2 O.sub.1j                                                               90.7 (3)                                       N.sub.1d CrN.sub.1e                                                                      176.1 (2)   O.sub.1i Na.sub.2 C.sub.4a                                                               109.3 (3)                                      N.sub.1d CrO.sub.1f                                                                      87.6 (2)    O.sub.1i Na.sub.2 C.sub.1e                                                               131.5 (2)                                      N.sub.1e CrO.sub.1f                                                                      88.5 (2)    O.sub.1j Na.sub.2 C.sub.4a                                                               103.2 (2)                                                            O.sub.1j Na.sub.2 C.sub.1e                                                               115.1 (3)                                      CrN.sub.1a C.sub.1a                                                                      128.7 (5)   C.sub.4a Na.sub.2 C.sub.1e                                                               103.9 (3)                                      CrN.sub.1a C.sub.4a                                                                      126.3 (5)                                                            CrN.sub.1b C.sub.1b                                                                      127.0 (4)   Na.sub.1 O.sub.1g C.sub.1g                                                               131.4 (6)                                      CrN.sub.1b C.sub.4b                                                                      127.3 (5)   Na.sub.1 O.sub.1g C.sub.4g                                                               124.0 (8)                                      CrN.sub.1c C.sub.1c                                                                      128.5 (5)   Na.sub.1 O.sub.1h C.sub.1h                                                               132.2 (7)                                      CrN.sub.1c C.sub.4c                                                                      126.7 (5)   Na.sub.1 O.sub.1h C.sub.4h                                                               116.6 (6)                                      CrN.sub.1d C.sub.1d                                                                      127.7 (5)   Na.sub.2 O.sub.1i C.sub.1i                                                               120.9 (8)                                      CrN.sub.1d C.sub.4d                                                                      125.7 (5)   Na.sub.2 O1iC.sub.4i                                                                     126.8 (7)                                      CrN.sub.1e C.sub.1e                                                                      127.7 (5)   Na.sub.2 O1jC.sub.1j                                                                     123.1 (6)                                      CrN.sub.1e C.sub.4e                                                                      126.2 (4)   Na.sub.2 O1jC.sub.4j                                                                     125.8 (5)                                      CrO.sub.1f C.sub. 1f                                                                     126.4 (4)   C.sub.1g O.sub.1g C.sub.4g                                                               104.3 (8)                                      CrO.sub.1f C.sub.4f                                                                      123.1 (5)   C.sub.1h O.sub.1h C.sub.4h                                                               108.9 (9)                                                            C.sub.1i O.sub.1i C.sub.4i                                                               107.8 (11)                                     C.sub.1a N.sub.1a C.sub.4a                                                               105.0 (6)   C.sub.1j O.sub.1j C.sub.4j                                                               107.7 (7)                                      C.sub.1b N.sub.1b C.sub.4b                                                               105.2 (5)                                                            C.sub.1c N.sub.1c C.sub.4c                                                               104.0 (5)   O.sub.1g C.sub.1g C.sub.2g                                                               111 (1)                                        C.sub.1d N.sub.1d C.sub.4d                                                               106.6 (6)   C.sub.1g C.sub.2g C.sub.3g                                                               103 (1)                                        C.sub.1e N.sub.1e C.sub.4e                                                               106.0 (6)   C.sub.2g C.sub.3g C.sub.4g                                                               103 (1)                                                              C.sub.3g C.sub.4g O.sub.1g                                                               110 (1)                                        C.sub.1f O.sub.1f C.sub.4f                                                               110.5 (6)   O.sub.1h C.sub.1h C.sub.2h                                                               106 (1)                                                              C.sub.1h C.sub.2h C.sub.3h                                                               106 (1)                                        N.sub.1a C.sub.1a C.sub.2a                                                               111.1 (7)   C.sub.2h C.sub.3h C.sub.4h                                                               109 (1)                                        C.sub.1a C.sub.2a C.sub.3a                                                               106.1 (8)   C.sub.3h C.sub.4h O.sub.1h                                                               106 (1)                                        C.sub.2a C.sub.3a C.sub.4a                                                               107.5 (7)   O.sub.1i C.sub.1i C.sub.2i                                                               110 (2)                                        C.sub.3a C.sub.4a N.sub.1a                                                               110.3 (7)   C.sub.1i C.sub.2i C.sub.3i                                                               105 (2)                                        N.sub.1b C.sub.1b C.sub.2b                                                               110.6 (7)   C.sub.2i C.sub.3i C.sub.4i                                                               106 (2)                                        C.sub.1b C.sub.2b C.sub.3b                                                               107.6 (8)   C.sub.3i C.sub.4i O.sub.1i                                                               107 (1)                                        C.sub.2b C.sub.3b C.sub.4b                                                               104.4 (7)   O.sub.1j C.sub.1j C.sub.2j                                                               106 (1)                                        C.sub.3b C.sub.4b N.sub.1b                                                               112.2 (7)   C.sub.1j C.sub.2j C.sub.3j                                                               109 (1)                                        N.sub.1c C.sub.1c C.sub.2c                                                               112.4 (7)   C.sub.2j C.sub.3j C.sub.4j                                                               104 (1)                                        C.sub.1c C.sub.2c C.sub.3c                                                               104.5 (7)   C.sub.3j C.sub.4j O.sub.1j                                                               108 (1)                                        C.sub.2c C.sub.3c C.sub.4c                                                               107.8 (7)                                                            C.sub.3c C.sub.4c N.sub.1c                                                               111.2 (7)   Na.sub.1 C.sub.1a N.sub.1a                                                               95.0 (4)                                       N.sub.1d C.sub.1d C.sub.2d                                                               109.0 (7)   Na.sub.1 C.sub.1a C.sub.2a                                                               106.7 (5)                                      C.sub.1d C.sub.2d C.sub.3d                                                               107.6 (8)   Na.sub.1 N.sub.1d Cr                                                                     107.7 (3)                                      C.sub.2d C.sub.3d C.sub.4d                                                               105.4 (8)   Na.sub.1 N.sub.1d C.sub.1d                                                               72.6 (4)                                       C.sub.3d C.sub.4d N.sub.1d                                                               111.5 (7)   Na.sub.1 N.sub.1d C.sub.4d                                                               86.4 (4)                                       N.sub.1e C.sub.1e C.sub.2e                                                               111.0 (7)   Na.sub.1 C.sub.1d N.sub.1d                                                               78.1 (4)                                       C.sub.1e C.sub.2e C.sub.3e                                                               105.2 (7)   Na.sub.1 C.sub.1d C.sub.2d                                                               85.1 (6)                                       C.sub.2e C.sub.3e C.sub.4e                                                               108.4 (8)                                                            C.sub.3e C.sub.4e N.sub.1e                                                               109.5 (7)   Na.sub.2 C.sub.4a N.sub.1a                                                               90.2 (3)                                                             Na.sub.2 C.sub.4a C.sub.3a                                                               104.0 (5)                                      O.sub.1f C.sub.1f C.sub.2f                                                               104.4 (7)   Na.sub.2 C.sub.1e N.sub.1e                                                               78.1 (4)                                       C.sub.1f C.sub.2f C.sub.3f                                                               105.0 (9)   Na.sub.2 C.sub.1e C.sub.2e                                                               91.7 (6)                                       C.sub.2f C.sub.3f C.sub.4f                                                               104.9 (9)                                                            C.sub.3f C.sub.4f O.sub.1f                                                               104.7 (7)                                                            ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIG. 6.                       

EXAMPLE VII

The product obtained from the reaction of sodium 2,5-dimethylpyrrolide and CrCl₂ used in the preparation of an active catalyst was a light blue solid, Product VI. 2,5-Dimethylpyrrole (5.0 ml/49.1 mmole) was mixed with excess sodium (40% dispersion in mineral spirits) in tetrahydrofuran (125 ml) at ambient temperature. The mixture was refluxed 12 hours under nitrogen then filtered to remove excess sodium. The sodium 2,5-dimethylpyrrolide was used in-site and combined with chromous chloride (3.03 g/24.7 mmole) at ambient temperature. The reaction mixture was refluxed under nitrogen for 48 hours. The gray-green solution was filtered (medium porosity frit) at ambient temperature and stripped of solvent under vacuum, then pumped dry under vacuum for 12 hours resulting in a gray/green solid. This gray/green solid was then washed with pentane resulting in a light blue solid, Product VI, which was collected by filtration. Product VI was used in the preparation of an active catalyst without further purification.

EXAMPLE VIII PREPARATION OF CATALYSTS

All polymerization runs were carried out in a two liter reactor under slurry (particle form) conditions. The diluent was isobutane and the reactor temperature was 90° C. Reactor pressure held at 550 psig during the polymerization, with ethylene being fed on demand.

The actual charging of the reactor was accomplished by the following method. After purging the reactor at 100° C. and a stream of nitrogen for at least 15 minutes, the reactor temperature was lowered to 90° C. and a preweighed amount of supported chromium pyrrolide catalyst was charged against a slight countercurrent of nitrogen. One liter of isobutane was then charge to the reactor and finally the reactor pressurized with ethylene.

The ethylene consumed was determined using a precalibrated ethylene flow meter. Samples of the liquid product mixture were taken after 30 minute run time without depressurizing the reactor. This was done by filling to 200-300 psig a steel sampling cylinder adapted to the reactor with a dip tube fitted with a fritted tip extending into the bottom of the reactor vessel. Samples taken this way were analyzed by gas chromatography and gas chromatography-mass spectrometry. Selectivities were normalized to 100%. Solid products were obtained by venting the reactor to atmosphere, separating by decantation of the liquids from the solid material. The solids were then dried at 100° C. in a vacuum oven and weighed. The yield of solid product was obtained by weighing the combined solid and catalyst residues and subtracting from this the preweighed catalyst charge. The yield of volatile products was obtained by subtracting the yield of solid products from the grams of ethylene consumed as recorded by the flow meter.

Activity typically ranged from 300-1500 g product/g catalyst/hour calculated for 30 minute run time, as shown in Table XVI. The product obtained typically was represented by 97-99.5% by weight liquids and 0.5-3% by weight polymer (wax). The liquid fraction was typically 85% hexenes, 11% decenes, 2% tetradecences, based on the total weight of the liquid fraction. The balance of the liquid product mixture was a trace level distribution of olefins typically totaling about 1-2% by weight of the product mixture, see Table XVII.

Active catalysts were prepared from the chromium pyrrolide complexes as follows. All toluene and/or pentane rinses used about 15 to about 30 mls of liquid.

Run 1: 0.158 g of Product V (prepared in THF solvent), which was heated to 80° C. for 4 hours under nitrogen flush to remove residual THF, was slurried with 15 ml toluene at ambient temperature. 9.0 ml of a 1M TEA in hexanes solution was added to the solution and stirred for 24 hours. The formation of a brown solution and the complete dissolution of Product V resulted immediately upon TEA addition. AlPO₄ (P/Al mole ratio=0.4) (2.00 g) was added to the solution and stirred for an additional 24 hours. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice with pentane. 0.3143 g of the catalyst was charged directly to the reactor for polymerization. 1.0 ml of a 0.5% TEA in heptanes solution was charged to the reactor after the catalyst charge but before the isobutane (reactor solvent) charge to purge feedstock poisons.

Run 2: 0.081 g of Product V (prepared in THF solvent), which was heated to 80° C. for 4 hours under nitrogen flush to remove residual THF, was slurried with 15 ml diethylbenzene at ambient temperature. 2.0 ml of a 1M TEA in hexanes solution was added to the solution and stirred for 24 hours. The formation of a brown solution and the complete dissolution of Product V resulted immediately upon TEA addition. AlPO₄ (P/Al mole ratio=0.4) (1.50 g) was added to the solution and stirred for an additional 1 hour. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with dimethylbenzene, and then twice with pentane. 0.4333 g of the catalyst was charged directly to the reactor for polymerization. 3.0 ml of a 0.5% TEA in heptanes solution was charged to the reactor after the catalyst charge but before the isobutane (reactor solvent) charge to purge feedstock poisons.

Run 3: 0.093 g of Product V (prepared in DME solvent) was slurried with 15 ml toluene at ambient temperature. 5.0 ml of a 1M TEA in hexanes solution was added to the solution and stirred for 24 hours. The formation of a brown solution and the complete dissolution of Product V resulted immediately upon TEA addition. AlPO₄ (P/Al mole ratio=0.4) (1.0 g) was added to the solution and stirred for an additional 24 hours. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice with pentane. 0.1564 g of the catalyst was charged directly to the reactor for polymerization. 3.0 ml of a 0.5% TEA in heptanes solution was charged to the reactor after the catalyst charge but before the isobutane (reactor solvent) charge to purge feedstock poisons.

Run 4: 0.080 g of Product I (prepared in THF solvent) was slurried with 15 ml toluene at ambient temperature. 6.0 ml of a 1M TEA in hexanes solution was added and the solution stirred for 16 hours. The formation of a brown solution and the complete dissolution of Product I resulted immediately upon TEA addition. AlPO₄ (P/Al mole ratio=0.4) (1.50 g) was added to the solution and stirred for an additional 16 hours. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice pentane. 1.1988 g of the catalyst was charged directly to the reactor for polymerization.

Run 5: 0.079 g of Product II (prepared in THF solvent) was slurried with 15 ml toluene at ambient temperature. 2.0 ml of a 1.9M TEA in toluene solution was added to the solution and stirred for 8 hours. The formation of a brown solution and the complete dissolution of Product II resulted immediately upon TEA addition. AlPO₄ (P/Al mole ratio=0.4) (0.50 g) was added to the solution and stirred for an additional 16 hours. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice with pentane. 0.4829 g of the catalyst was charged directly to the reactor for polymerization.

Run 6: 0.071 g of Product V (prepared in THF solvent), which was heated to 80° C. for 4 hours under nitrogen flush to remove residual THF, was slurried with 15 ml toluene at ambient temperature. 2.0 ml of a 1M TEA in hexanes solution was added to the solution and stirred for 1 hour. The formation of a brown solution and the complete dissolution of Product V resulted immediately upon TEA addition. SiO₂ (2.52 g) was added to the solution and stirred for an additional 2 minutes. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice with pentane. All of the catalyst was charged directly to the reactor for polymerization.

Run 7: 0.103 g of Product II (prepared in THF solvent) was slurried with 15 ml toluene at ambient temperature. 1.0 ml of a 1.9M TEA in toluene solution was added to the solution and stirred for 10 minutes. The formation of a brown solution and the complete dissolution of Product II resulted immediately upon TEA addition. Al₂ O₃ (2.27 g) was added to the solution and stirred for an additional 2 minutes. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice with pentane. 1.2926 g of the catalyst was charged directly to the reactor for polymerization.

Run 8: 0.120 g of Product I (prepared in THF solvent) was slurried with 15 ml toluene at ambient temperature. 2.0 ml of a 1M TEA in hexanes solution was added to the solution and stirred for 2 days. The formation of a brown solution and the complete dissolution of Product I resulted immediately upon TEA addition. SiO₂ (1.0 g) was added to the solution and stirred for an additional 3 weeks. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice with pentane. All of the catalyst was charged directly to the reactor for polymerization.

Run 9: 0.106 g of Product III (prepared in THF solvent) was slurried with 15 ml toluene at ambient temperature. 2.5 ml of a 1.9M TEA in toluene solution was added to the solution and stirred for 2 hours. The formation of a brown solution and the complete dissolution of Product III resulted immediately upon TEA addition. AlPO₄ (P/Al mole ratio=0.4) (0.65 g) was added to the solution and stirred for an additional 2 hours. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice with pentane. All of the catalyst was charged directly to the reactor for polymerization. 1.5 ml of a 1.0% TEA in pentane solution was charged to the reactor after the catalyst charge but before the isobutane (reactor solvent) charge to purge feedstock poisons.

Run 10: 0.030 g of Product V (prepared in THF solvent) which was heated to 80° C. for 4 hours under nitrogen flush to remove residual THF was slurried with 15 ml toluene at ambient temperature. 3.0 ml of a 1M TEA in hexanes solution was added to the solution and stirred for 16 hours. The formation of a brown solution and the complete dissolution of Product V resulted immediately upon TEA addition. AlPO₄ (P/Al=0.09) (2.0 g) was added to the solution and stirred for an additional 16 hours. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice with pentane. 0.322/g of catalyst was charged directly to the reactor for polymerization.

Run 11: 0.067 g of Product V (prepared in THF solvent) was slurried with 15 ml pentane at ambient temperature. 4.0 ml of a 1M TEA in hexanes solution was added to the solution and stirred for 24 hours. The formation of a brown solution and the complete dissolution of Product V resulted immediately upon TEA addition. AlPO₄ (P/Al mole ratio=0.4) (1.0 g) was added to the solution and stirred for an additional 24 hours. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with pentane. All of the catalyst was charged directly to the reactor for polymerization. 3.0 ml of a 0.5% TEA in heptanes solution was charged to the reactor after the catalyst charge but before the isobutane (reactor solvent) charge to purge feedstock poisons.

Run 12: 0.073 g of Product V (prepared in THF solvent), which was heated to 80° C. for 4 hours under nitrogen flush to remove residual THF, was slurried with 15 ml toluene at ambient temperature. 6.0 ml of a 1M TEA in hexanes solution was added and the solution stirred for 24 hours. The formation of a brown solution and the complete dissolution of Product V resulted immediately upon TEA addition. P/SiO₂ (7.0 g) was added to the solution and stirred for an additional 24 hours which nearly decolorized it. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice with pentane. 2.85 g of catalyst was charged directly to the reactor for polymerization.

Run 13: 0.125 g or Product II was slurried with 15 ml diethylbenzene at ambient temperature. 9.0 ml of a 1M TEA in hexanes solution was added to the solution and stirred for 8 hours. The formation of a brown solution and the complete dissolution of Product II resulted immediately upon TEA addition. F/Al₂ O₃ (2.0 g) was added to the solution and stirred for an additional 12 hours. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice with pentane. 0.5477 g of catalyst was charged directly to the reactor for polymerization.

Run 14: 0.125 g of Product VI was slurried with 15 ml toluene at ambient temperature. 1.5 ml of a 1M TEA in hexanes solution was added and the solution stirred for 10 minutes. The formation of a red/brown solution and the complete dissolution of Product VI resulted immediately upon TEA addition. SiO₂ (2.0 g) was added to the solution and stirred for an additional 1 minute which nearly decolorized it. The supported silica catalyst was filtered from the solution as a red/brown solid, rinsed twice with toluene, and then twice with pentane. All of the catalyst was charged directly to the reactor for polymerization.

Run 15: 0.30 g of Product V (prepared in DME solvent) was dissolved with 15 ml of dimethoxyethane forming a green solution. This solution was then mixed with 0.6 g of AlPO₄ (P/Al₄ mole ratio=0.4) (2.00 g) and the mixture was stirred 1 hour. The green supported material was filtered from the solution, rinsed with dimethoxyethane and dried with a nitrogen purge at 90° C. This material was then stirred with 15 ml of toluene and 3 ml of triethylaluminum (Aldrich 1.0M, hexanes) for an additional 3 hours. The brown supported catalyst was collected by filtration, rinsed with pentane, and dried under vacuum. 0.4609 g of the catalyst was charged directly to the reactor for polymerization. 3.0 ml of a 0.5% TEA in heptanes solution was charged to the reactor after the catalyst charge but before the isobutane reactor solvent) charge to purge feedstock poisons.

Run 16: 0.058 g of Product V (prepared in THF solvent) which was heated to 80° C. for 4 hours under nitrogen flush to remove residual THF was slurried with 15 ml benzene at ambient temperature. 4.0 ml of a 1M TEA in hexanes solution was added and the solution stirred for 2 hours. The formation of a brown solution and the complete dissolution of Product V resulted immediately upon TEA addition. AlPO₄ (P/Al mole ratio=0.4) (1.0 g) was added to the solution and stirred for 1 hour. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with benzene, and then twice with pentane. All of the catalyst was charged directly to the reactor for polymerization. 3.0 ml of a 0.5% TEA in heptanes solution was charged to the reactor after the catalyst charge but before the isobutane (reactor solvent) charge to purge feedstock poisons.

Run 17: 0.1610 g of Product I was charged directly to the reactor at 90° C. The reactor was charged with 1 liter isobutane and pressurized to 550 psig with ethylene. No ethylene consumption was detected, therefore 50 psig of dihydrogen was charged to the reactor which did not initiate ethylene consumption. Ethylene consumption was initiated after 2.0 ml of 1M TEA in hexanes solution was charged.

Run 18: 0.3528 g of Product VI was charged directly to the reactor at 90° C. The reactor was charged with 1 liter isobutane and pressurized to 550 psig with ethylene. No ethylene consumption was detected, therefore 2.0 ml of a 1M TEA in hexanes solution was charged which did initiate ethylene consumption.

Run 19: 0.3482 g of Product VI was charged directly to the reactor at 90° C. The reactor was also charged with 2.0 ml of a 1M TEA in hexanes solution prior to a 1 liter isobutane charge. The reactor was then pressurized to 550 psig with ethylene. No ethylene consumption was detected, therefore 30 psi of dihydrogen was charged to the reactor which initiated ethylene consumption.

Run 20: 0.202 g of Product V (prepared in dimethoxyethane (DME) solvent), 6.0 ml of a 1.9M TEA in toluene solution, and 2.0 g of AlPO₄ (P/Al mole ratio=0.4) were mixed with 15 ml toluene at ambient temperature. The formation of a brown solution and the complete dissolution of Product V resulted immediately upon mixing. The brown solution was stirred for 48 hours. The supported catalyst was filtered from the solution as a brown solid, rinsed twice with toluene, and then twice with pentane. 0.0671 g of the catalyst was charged directly to the reactor for polymerization. 1.0 ml of a 0.5% TEA in heptanes solution was charged to the reactor after the catalyst charge but before the isobutane (reactor solvent) charge to purge feedstock poisons.

The data in Table XVI show that the inventive chromium compounds can be used either supported (Runs 1-16, 20) or unsupported (Runs 17-19) to polymerize and/or trimerize olefins. Furthermore, conditions can be varied to increase the amount of trimer product (Runs 1-5 and 9) or to have a higher yield of solid, or polymer, product (Runs 6, 7, and 13). Runs 1, 3, and 20 demonstrate that high activities are attainable.

                                      TABLE XVI                                    __________________________________________________________________________     Run.sup.a                                                                         Catalyst     Support.sup.b                                                                         Products      Activity.sup.c                            __________________________________________________________________________      1 (V)/TEA/Toluene                                                                             AlPO.sub.4                                                                            98.4% liquids, 1.6% solids                                                                   1030                                       2 (V)/TEA/Diethylbenzene                                                                      AlPO.sub.4                                                                            99.4% liquids, 0.6% solids                                                                   730                                        3 (V)/TEA/Toluene                                                                             AlPO.sub.4                                                                            99.4% liquids, 0.6% solids                                                                   1450                                       4 (I)/TEA/Toluene                                                                             AlPO.sub.4                                                                            98.6% liquids, 1.4% solids                                                                   .sup. 360.sup.d                            5 (II)/TEA/Toluene                                                                            AlPO.sub.4                                                                            98.2% liquids, 1.8% solids                                                                   580                                        6 (V)/TEA/Toluene                                                                             SiO.sub.2                                                                             89.0% liquids, 11.0% solids                                                                   80                                        7 (II)/TEA/Toluene                                                                            Al.sub.2 O.sub.3                                                                      55.8% liquids, 44.2% solids                                                                   50                                        8 (I)/TEA/Toluene                                                                             SiO.sub.2                                                                             93.3% liquids, 6.7% solids                                                                   400                                        9 (III)/TEA/Toluene                                                                           AlPO.sub.4                                                                            99.8% liquids, 0.2% solids                                                                   100                                       10 (V)/TEA/Toluene                                                                             AlPO.sub.4 (.9)                                                                       96.8% liquids, 3.2% solids                                                                   930                                       11 (V)/TEA/Pentane                                                                             AlPO.sub.4                                                                            (trace) liquids, (trace) solids                                                              unreactive                                12 (V)/TEA/Toluene                                                                             P/SiO.sub.2                                                                           98.1% liquids, 1.9% solids                                                                    90                                       13 (II)/TEA/Diethylbenzene                                                                     F/Al.sub.2 O.sub.3                                                                    88.0% liquids, 12.0% solids                                                                  300                                       14 (VI)/TEA/Toluene                                                                            SiO.sub.2                                                                             94.3% liquids, 5.7% solids                                                                    40                                       15 (V)/DME      AlPO.sub.4                                                                            98.0% liquids, 2.0% solids                                                                   550                                       16 (V)/TEA/Benzene                                                                             AlPO.sub.4                                                                            99.1% liquids, 0.9% solids                                                                   500                                       17 (I)/TEA      unsupported                                                                           98.3% liquids, 1.7% solids                                                                   340                                       18 (VI)/TEA     unsupported                                                                           99.4% liquids, 0.6% solids                                                                   180                                       19 (VI)/TEA     unsupported                                                                           98.1% liquids, 1.9% solids                                                                   230                                       20 (V)/TEA      AlPO.sub.4                                                                            99.5% liquids, 0.5% solids                                                                   2760                                      __________________________________________________________________________      .sup.a All runs were made at 90° C., isobutane solvent, 550 psi         total pressure.                                                                .sup.b P/Al mold ratio = 0.4; except Run 10 whereby P/Al mole ratio = 0.9      .sup.c Grams product/grams catalyst/hour based on 30 min. run times.           .sup.d Believed to be lower than actual due to experimental error; actual      value believe to be near 2000.                                           

                  TABLE XVII                                                       ______________________________________                                         Run  C4     1-hexene C6   C8   C10  C12  C14  C16-C28                          ______________________________________                                         1    0.05   81.92    7.76 0.49 9.12 0.09 0.52 .05                              2    0.10   78.80    7.49 0.58 11.36                                                                               0.10 1.01 .56                              3    0.06   82.19    7.68 0.45 8.85 0.08 0.58 .11                              5    0.10   83.40    7.08 0.62 8.08 0.05 0.42 .25                              6    0.55   78.70    5.52 1.84 11.24                                                                               0.42 1.26 .47                              16   0.06   72.85    13.61                                                                               0.31 12.06                                                                               0.09 0.93 .09                              19   6.03   71.66    6.09 3.61 9.42 1.17 1.41 .61                              ______________________________________                                    

EXAMPLE IX

Single crystal x-ray structures were obtained for Cr(NC₄ H₄)₃ Cl(O₂ C₂ H₄ (CH₃)₂)₃ Na, shown in FIGS. 7 and 8, and Cr(NC₄ H₄)₃ Cl(O₂ C₂ H₄ (CH₃)₂), and shown in FIG. 9. These crystals were obtained in accordance with the procedure given in Example III. However, x-ray quality crystals were obtained after the dark green, filtered solution was maintained at ambient temperature and pressure under an inert atmosphere, nitrogen, for a time of about 2 days. Analysis calculated for C₂₄ H₄₂ N₃ O₆ CrNaCl: C, 49-78; H, 7.31; N, 7.26% by weight. Found: C, 49.80; H 7.39; N, 7.18% by weight.

The description of the single-crystal sample and mounting used for data collection are as follows:

Color: Green/black

Shape: Rectangular parallelepiped

Dimensions: 0.44×0.62×0.62 mm

Crystal Mount: Crystal was glued to the inside of a thin-walled glass capillary and sealed under N₂.

Crystal Orientation: Crystal was oriented with its longer edges nearly parallel to the phi axis of the diffractometer.

Width at Half-height from ω Scans: 0.38°

The space group and cell data are as follows:

Crystal System: Monoclinic

Space Group and Number:² P2₁ /c--C_(2h) ⁵ (No. 14)

Number of Computer-Centered Reflections Used in the Least-Squares Refinement of the Cell Dimensions:

15 20°>25° °C.=20±1

    ______________________________________                                         Lattice Constants with esd's:                                                  ______________________________________                                         a = 8.135(2)Å                                                                            α = 90.00°                                                                     V = 3026(1)Å.sup.3                              b = 22.337(5)Å                                                                           β = 91.67(2)°                                                                   Z = 4                                               c = 16.667(4)Å                                                                           γ = 90.00°                                                                     λ = 0.71073Å                             ______________________________________                                    

Molecular Weight: 579.05 amu

Calculated Density: 1.271 g/cn⁻³

Linear Absorption Coefficient:^(3a) 0.51 mm⁻¹

Tables XVIII-XXII list the resultant parameters used to generate the molecular structures shown in FIGS. 7 and 8.

                  TABLE XVIII                                                      ______________________________________                                         Atomic Coordinates for Nonhydrogen Atoms in                                    Crystalline [Cr(NC.sub.4 H.sub.4).sub.3 (Cl)(O.sub.2 C.sub.2 H.sub.4           (CH.sub.3).sub.2).sub.3 Na].sup.a                                                                         Equivalent Isotropic                                Atom  Fractional Coordinates                                                                              Thermal Parameter,                                  Type.sup.b                                                                           10.sup.4 x                                                                               10.sup.4 y                                                                               10.sup.4 z                                                                            B, Å.sup.2 × 10.sup.c               ______________________________________                                         Cr    -1030 (1) 559 (1)   3005 (1)                                                                              30 (1)                                        Cl    135 (1)   -26 (1)   1981 (1)                                                                              41 (1)                                        Na    -2167 (2) -1011 (1) 1832 (1)                                                                              46 (1)                                        N.sub.1                                                                              -3062 (4) 65 (2)    2907 (2)                                                                              35 (1)                                        C.sub.11                                                                             -4107 (5) 63 (2)    2251 (3)                                                                              40 (1)                                        C.sub.12                                                                             -5189 (5) -409 (2)  2291 (3)                                                                              51 (1)                                        C.sub.13                                                                             -4810 (5) -713 (2)  2998 (3)                                                                              51 (1)                                        C.sub.14                                                                             -3512 (5) -414 (2)  3361 (3)                                                                              46 (1)                                        N.sub.2                                                                              -1817 (4) 1027 (2)  3950 (2)                                                                              37 (1)                                        C.sub.21                                                                             -1188 (6) 1558 (2)  4234 (3)                                                                              47 (1)                                        C.sub.22                                                                             -2205 (7) 1790 (2)  4799 (3)                                                                              60 (2)                                        C.sub.23                                                                             -3499 (7) 1398 (2)  4874 (3)                                                                              60 (2)                                        C.sub.24                                                                             -3248 (5) 934 (2)   4349 (2)                                                                              43 (1)                                        N.sub.3                                                                              -1892 (4) 1185 (2)  2260 (2)                                                                              35 (1)                                        C.sub.31                                                                             -3100 (5) 1588 (2)  2434 (3)                                                                              41 (1)                                        C.sub.32                                                                             -3573 (6) 1901 (2)  1757 (3)                                                                              53 (1)                                        C.sub.33                                                                             -2631 (6) 1686 (2)  1130 (3)                                                                              51 (1)                                        C.sub.34                                                                             -1620 (6) 1249 (2)  1453 (3)                                                                              46 (1)                                        O.sub.1a                                                                             1317 (3)  971 (1)   3154 (2)                                                                              40 (1)                                        O.sub.2a                                                                             153 (3)   -12 (1)   3878 (2)                                                                              40 (1)                                        C.sub.1a                                                                             2459 (5)  631 (2)   3651 (3)                                                                              53 (1)                                        C.sub.2a                                                                             1443 (6)  329 (2)   4268 (3)                                                                              53 (1)                                        C.sub.3a                                                                             2156 (6)  1247 (2)  2495 (3)                                                                              58 (2)                                        C.sub.4a                                                                             653 (6)   -625 (2)  3733 (3)                                                                              49 (1)                                        O.sub.1b                                                                             -2558 (4) -783 (2)  398 (2)                                                                               62 (1)                                        O.sub.2b                                                                             -3877 (5) -1772 (2) 1111 (2)                                                                              76 (1)                                        C.sub.1b                                                                             -3618 (9) -1166 (3) -25 (4)                                                                               89 (2)                                        C.sub.2b                                                                             -3627 (9) -1765 (3) 302 (4)                                                                               83 (2)                                        C.sub.3b                                                                             -2410 (8) -207 (3)  61 (4) 79 (2)                                        C.sub.4b                                                                             -4149 (9) -2328 (3) 1440 (5)                                                                              106 (3)                                       O.sub.1c                                                                             -1334 (4) -1823 (2) 2911 (2)                                                                              65 (1)                                        O.sub.2c                                                                             235 (5)   -1589 (2) 1529 (3)                                                                              87 (2)                                        C.sub.1c                                                                             71 (7)    -2144 (3) 2724 (4)                                                                              83 (2)                                        C.sub.2c                                                                             951 (8)   -1913 (4) 2067 (4)                                                                              107 (3)                                       C.sub.3c                                                                             -2090 (8) -2017 (3) 3614 (4)                                                                              83 (2)                                        C.sub.4c                                                                             1224 (8)  -1393 (3) 900 (4)                                                                               88 (2)                                        ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIG. 7.                             .sup.c This is onethird of the trace of the orthogonalized B.sub.ij            tensor.                                                                  

                  TABLE XIX                                                        ______________________________________                                         Anisotropic Thermal Parameters for Nonhydrogen Atoms                           in Crystalline [Cr(NC.sub.4 H.sub.4).sub.3 (Cl)(O.sub.2 C.sub.2 H.sub.4        (CH.sub.3).sub.2).sub.3 Na].sup.a,b                                            Atom  Anisotropic Thermal Parameter (Å.sup.2 × 10)                   Type.sup.c                                                                           B.sub.11                                                                               B.sub.22                                                                               B.sub.33                                                                             B.sub.12                                                                              B.sub.13                                                                              B.sub.23                             ______________________________________                                         Cr    28 (1)  31 (1)  30 (1)                                                                               2 (1)  -0 (1) -2 (1)                               Cl    39 (1)  43 (1)  41 (1)                                                                               2 (1)  5 (1)  -9 (1)                               Na    47 (1)  48 (1)  44 (1)                                                                               0 (1)  3 (1)  -4 (1)                               N.sub.1                                                                              31 (1)  39 (2)  35 (2)                                                                               0 (1)  2 (1)  -3 (1)                               C.sub.11                                                                             31 (2)  47 (2)  41 (2)                                                                               0 (2)  -1 (2) -7 (2)                               C.sub.12                                                                             33 (2)  59 (3)  61 (3)                                                                               -3 (2) -4 (2) -16 (2)                              C.sub.13                                                                             35 (2)  39 (2)  79 (3)                                                                               -6 (2) 8 (2)  3 (2)                                C.sub.14                                                                             39 (2)  45 (2)  54 (2)                                                                               1 (2)  2 (2)  10 (2)                               N.sub.2                                                                              36 (2)  38 (2)  36 (2)                                                                               7 (1)  -3 (1) -8 (1)                               C.sub.21                                                                             55 (2)  38 (2)  47 (2)                                                                               9 (2)  -6 (2) -5 (2)                               C.sub.22                                                                             88 (3)  46 (3)  44 (2)                                                                               32 (2) -9 (2) -12 (2)                              C.sub.23                                                                             65 (3)  74 (3)  42 (2)                                                                               32 (2) 7 (2)  0 (2)                                C.sub.24                                                                             37 (2)  55 (2)  37 (2)                                                                               14 (2) -0 (2) 1 (2)                                N.sub.3                                                                              38 (2)  35 (2)  32 (2)                                                                               3 (1)  0 (1)  -0 (1)                               C.sub.31                                                                             35 (2)  43 (2)  43 (2)                                                                               6 (2)  -3 (2) 1 (2)                                C.sub.32                                                                             52 (2)  47 (2)  58 (3)                                                                               8 (2)  -11 (2)                                                                               6 (2)                                C.sub.33                                                                             62 (3)  51 (3)  39 (2)                                                                               -2 (2) -8 (2) 12 (2)                               C.sub.34                                                                             52 (2)  45 (2)  40 (2)                                                                               -1 (2) 2 (2)  2 (2)                                O.sub.1a                                                                             32 (1)  40 (1)  50 (2)                                                                               -1 (1) -3 (1) -5 (1)                               O.sub.2a                                                                             40 (1)  38 (1)  41 (1)                                                                               6 (1)  -7 (1) -1 (1)                               C.sub.1a                                                                             33 (2)  50 (3)  73 (3)                                                                               4 (2)  -13 (2)                                                                               -10 (2)                              C.sub.2a                                                                             53 (2)  55 (3)  51 (2)                                                                               10 (2) -24 (2)                                                                               -10 (2)                              C.sub.3a                                                                             45 (2)  53 (3)  76 (3)                                                                               -15 (2)                                                                               8 (2)  -5 (3)                               C.sub.4a                                                                             50 (2)  40 (2)  58 (3)                                                                               12 (2) -8 (2) -1 (2)                               O.sub.1b                                                                             76 (2)  63 (2)  47 (2)                                                                               -14 (2)                                                                               -5 (2) 1 (2)                                O.sub.2b                                                                             101 (3) 62 (2)  63 (2)                                                                               -28 (2)                                                                               -5 (2) -2 (2)                               C.sub.1b                                                                             120 (5) 91 (4)  56 (3)                                                                               -29 (4)                                                                               -25 (3)                                                                               -3 (3)                               C.sub.2b                                                                             116 (5) 64 (3)  68 (4)                                                                               -18 (3)                                                                               -24 (3)                                                                               -12 (3)                              C.sub.3b                                                                             81 (4)  84 (4)  72 (4)                                                                               -9 (3) -1 (3) 19 (3)                               C.sub.4b                                                                             118 (5) 84 (4)  113 (5)                                                                              -51 (4)                                                                               -38 (4)                                                                               29 (4)                               O.sub.1c                                                                             61 (2)  64 (2)  70 (2)                                                                               8 (2)  0 (2)  4 (2)                                O.sub.2c                                                                             74 (2)  76 (3)  112 (3)                                                                              29 (2) 31 (2) 30 (2)                               C.sub.1c                                                                             73 (3)  65 (3)  113 (5)                                                                              23 (3) 9 (3)  25 (3)                               C.sub.2c                                                                             83 (4)  143 (6) 96 (5)                                                                               61 (4) 24 (4) 14 (5)                               C.sub.3c                                                                             84 (4)  64 (3)  101 (5)                                                                              -8 (3) 3 (4)  16 (3)                               C.sub.4c                                                                             77 (4)  98 (5)  90 (5)                                                                               13 (3) 29 (3) -5 (4)                               ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b The form of the anisotropic thermal perameter is given in referenc      8 on page 6 of the crystal structure analysis report.                          .sup.c Atoms are labeled in agreement with FIG. 7.                       

                  TABLE XX                                                         ______________________________________                                         Atomic Coordinates for Hydrogen Atoms in Crystalline                           [Cr(NC.sub.4 H.sub.4).sub.3 (Cl)(O.sub.2 C.sub.2 H.sub.4 (CH.sub.3).sub.2)     .sub.3 Na].sup.a                                                               Atom        Fractional Coordinates                                             Type.sup.b  10.sup.4 x     10.sup.4 y                                                                           10.sup.4 z                                    ______________________________________                                         H.sub.11    -4089          350   1823                                          H.sub.12    -6043          -509  1905                                          H.sub.13    -5349          -1064 3195                                          H.sub.14    -2993          -526  3863                                          H.sub.21    -188           1740  4063                                          H.sub.22    -2044          2158  5089                                          H.sub.23    -4404          1441  5226                                          H.sub.24    -3967          597   4273                                          H.sub.31    -3554          1644  2954                                          H.sub.32    -4392          2210  1720                                          H.sub.33    -2680          1817  581                                           H.sub.34    -840           1021  1159                                          H.sub.1aa   3014           339   3336                                          H.sub.1ab   3254           892   3906                                          H.sub.2aa   967            626   4606                                          H.sub.2ab   2127           67    4588                                          H.sub.3aa   1391           1487  2185                                          H.sub.3ab   2589           938   2162                                          H.sub.3ac   3040           1495  2696                                          H.sub.4aa   -256           -834  3484                                          H.sub.4ab   926            -806  4242                                          H.sub.4ac   1586           -646  3395                                          H.sub.1ba   -4712          -1006 -11                                           H.sub.1bb   -3277          -1186 -570                                          H.sub.2ba   -2588          -1951 204                                           H.sub.2bb   -4492          -1988 37                                            H.sub.3ba   -1696          26    407                                           H.sub.3bb   -3461          -14   7                                             H.sub.3bc   -1935          -243  -458                                          H.sub.4ba   -4380          -2289 2000                                          H.sub.4bb   -3108          -2524 1385                                          H.sub.4bc   -4998          -2561 1178                                          H.sub.1ca   795            -2146 3189                                          H.sub.1cb   -255           -2547 2596                                          H.sub.2ca   1398           -2252 1795                                          H.sub.2cb   1831           -1676 2294                                          H.sub.3ca   -3168          -1848 3661                                          H.sub.3cb   -1397          -1884 4055                                          H.sub.3cc   -2164          -2446 3624                                          H.sub.4ca   456            -1357 454                                           H.sub.4cb   2033           -1690 780                                           H.sub.4cc   1756           -1015 996                                           ______________________________________                                          .sup.a The 6 methyl groups were refined as rigid rotors with                   sp.sup.3hydridized geometry and C--H bond lengths of 0.96Å. The            initial orientation of each methyl group was determined from difference        Fourier positions for the hydrogen atoms. The final orientation of each        methyl group was determined by three rotational parameters. The refined        positions for the rigid rotor methyl groups gave O--C--H angles which          ranged from 103° to 115°. The                                    remaining hydrogen atoms were included in the structure factor                 calculations as idealized atoms (assuming sp.sup.2 or                          sp.sup.3hybridization of the carbon atoms and a C--H bond length of            0.96Å) "riding" on their respective carbon atoms. The isotropic            thermal parameter of each hydrogen was fixed at 1.2 times the equivalent       isotropic thermal parameter of the carbon atom to which it is covalently       bonded.                                                                        .sup.b Hydrogens are labeled with the same subscripts as their carbon          atoms with an additional literal subscript (a, b or c) where necessary to      distinguish between hydrogen atoms bonded to the same carbon.            

                  TABLE XXI                                                        ______________________________________                                         Bond Lengths Involving Nonhydrogen Atoms in                                    Crystalline [Cr(NC.sub.4 H.sub.4).sub.3 (Cl)(O.sub.2 C.sub.2 H.sub.4           (CH.sub.3).sub.2).sub.3 Na].sup.a                                              Type.sup.b                                                                               Length, Å                                                                               Type.sup.b                                                                              Length, Å                                  ______________________________________                                         Cr--Cl    2.369 (1)    Cr--N.sub.1                                                                             1.990 (3)                                                             Cr--N.sub.2                                                                             2.010 (3)                                      Cr--O.sub.1a                                                                             2.128 (3)    Cr--N.sub.3                                                                             1.986 (3)                                      Cr--O.sub.2a                                                                             2.142 (3)                                                            N.sub.1 --C.sub.11                                                                       1.365 (5)    C.sub.11 --C.sub.12                                                                     1.376 (6)                                      N.sub.1 --C.sub.14                                                                       1.366 (6)    C.sub.12 --C.sub.13                                                                     1.386 (7)                                      N.sub.2 --C.sub.21                                                                       1.370 (6)    C.sub.13 --C.sub.14                                                                     1.376 (6)                                      N.sub.2 --C.sub.24                                                                       1.374 (5)    C.sub.21 --C.sub.22                                                                     1.373 (7)                                      N.sub.3 --C.sub.31                                                                       1.370 (5)    C.sub.22 --C.sub.23                                                                     1.377 (8)                                      N.sub.3 --C.sub.34                                                                       1.376 (6)    C.sub.23 --C.sub.24                                                                     1.375 (7)                                                             C.sub.31 --C.sub.32                                                                     1.373 (7)                                      O.sub.1a --C.sub.1a                                                                      1.443 (5)    C.sub.32 --C.sub.33                                                                     1.399 (7)                                      O.sub.1a --C.sub.3a                                                                      1.448 (6)    C.sub.33 --C.sub.34                                                                     1.375 (7)                                      O.sub.2a --C.sub.2a                                                                      1.437 (5)                                                            O.sub.2a --C.sub.4a                                                                      1.450 (5)    C.sub.1a --C.sub.2a                                                                     1.498 (7)                                      O.sub.1b --C.sub.1b                                                                      1.391 (8)    C.sub.1b --C.sub.2b                                                                     1.445 (9)                                      O.sub.1b --C.sub.3b                                                                      1.410 (7)    C.sub.1c --C.sub.2c                                                                      1.422 (10)                                    O.sub.2b --C.sub.2b                                                                      1.370 (7)                                                            O.sub.2b --C.sub.4b                                                                      1.379 (8)    Na . . . Cr                                                                             4.108 (2)                                      O.sub.1c --C.sub.1c                                                                      1.392 (7)                                                            O.sub.1c --C.sub.3c                                                                      1.408 (8)    Na--Cl   2.896 (2)                                      O.sub.2c --C.sub.2c                                                                      1.278 (9)                                                            O.sub.2c --C.sub.4c                                                                      1.409 (8)    Na--N.sub.1                                                                             3.098 (4)                                      Na--C.sub.11                                                                             2.967 (5)    Na--O.sub.1b                                                                            2.454 (4)                                      Na--C.sub.12                                                                             2.924 (5)    Na--O.sub.2b                                                                            2.483 (4)                                      Na--C.sub.13                                                                             3.015 (5)    Na--O.sub.1c                                                                            2.629 (5)                                      Na--C.sub.14                                                                             3.104 (5)    Na--O.sub.2c                                                                            2.408 (5)                                      Na--C.sub.g1.sup.c                                                                       2.788 (-)                                                            ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIG. 7.                             .sup.c The symbol C.sub.g1 is used to designated the center of gravity fo      the fivemembered ring containing N.sub.1, C.sub.11, C.sub.12, C.sub.13,        and C.sub.14 ; this value is therefore listed without an estimated             standard deviation.                                                      

                  TABLE XXII                                                       ______________________________________                                         Bond Angles Involving Nonhydrogen Atoms in                                     Crystalline [Cr(NC.sub.4 H.sub.4).sub.3 (Cl)(O.sub.2 C.sub.2 H.sub.4           (CH.sub.3).sub.2).sub.3 Na].sup.a                                              Type.sup.b                                                                               Angle, deg. Type.sup.b                                                                               Angle, deg.                                    ______________________________________                                         ClCrN.sub.1                                                                               89.1 (1)   ClCrN.sub.2                                                                              173.9 (1)                                      N.sub.1 CrN.sub.2                                                                         94.0 (1)   ClCrN.sub.3                                                                               94.5 (1)                                      N.sub.1 CrN.sub.3                                                                         93.5 (1)   N.sub.2 CrN.sub.3                                                                         90.5 (1)                                      ClCrO.sub.1a                                                                              86.9 (1)   N.sub.1 CrO.sub.1a                                                                       171.9 (1)                                      N.sub.2 CrO.sub.1a                                                                        89.4 (1)   N.sub.3 CrO.sub.1a                                                                        93.8 (1)                                      ClCrO.sub.2a                                                                              88.9 (1)   N.sub.1 CrO.sub.2a                                                                        94.7 (1)                                      N.sub.2 CrO.sub.2a                                                                        85.7 (1)   N.sub.3 CrO.sub.2a                                                                       171.2 (1)                                      O.sub.1a CrO.sub.2a                                                                       78.2 (1)                                                            CrN.sub.1 C.sub.11                                                                       124.4 (3)   C.sub.11 N.sub.1 C.sub.14                                                                105.7 (3)                                      CrN.sub.1 C.sub.14                                                                       128.6 (3)   C.sub.21 N.sub.2 C.sub.24                                                                106.1 (4)                                      CrN.sub.2 C.sub.21                                                                       126.6 (3)   C.sub.31 N.sub.3 C.sub.34                                                                106.0 (3)                                      CrN.sub.2 C.sub.24                                                                       126.5 (3)                                                            CrN.sub.3 C.sub.31                                                                       125.0 (3)   CrO.sub.1a C.sub. 1a                                                                     113.5 (2)                                      CrN.sub.3 C.sub.34                                                                       128.3 (3)   Cro.sub.1a C.sub.3a                                                                      122.5 (3)                                                            C.sub.1a O.sub.1a C.sub.3a                                                               110.5 (3)                                      N.sub.1 C.sub.11 C.sub.12                                                                110.3 (4)   CrO.sub.2a C.sub.2a                                                                      107.4 (2)                                      C.sub.11 C.sub.12 C.sub.13                                                               106.9 (4)   CrO.sub.2a C.sub.4a                                                                      124.9 (3)                                      C.sub.12 C.sub.13 C.sub.14                                                               106.5 (4)   C.sub.2a O.sub.2a C.sub.4a                                                               111.8 (3)                                      N.sub.1 C.sub.14 C.sub.13                                                                110.6 (4)   C.sub.1b O.sub.1b C.sub.3b                                                               114.7 (4)                                      N.sub.2 C.sub.21 C.sub.22                                                                109.7 (4)   C.sub.2b O.sub.2b C.sub.4b                                                               115.6 (5)                                      C.sub.21 C.sub.22 C.sub.23                                                               107.4 (4)   C.sub.1c O.sub.1c C.sub.3c                                                               114.2 (5)                                      C.sub.22 C.sub.23 C.sub.24                                                               107.1 (4)   C.sub.2c O.sub.2c C.sub.4c                                                               116.0 (5)                                      N.sub.2 C.sub.24 C.sub.23                                                                109.7 (4)                                                            N.sub.3 C.sub.31 C.sub.32                                                                110.3 (4)   O.sub.1a C.sub.1a C.sub.2a                                                               105.8 (3)                                      C.sub.31 C.sub.32 C.sub.33                                                               107.0 (4)   O.sub.2a C.sub.2a C.sub.1a                                                               109.8 (4)                                      C.sub.32 C.sub.33 C.sub.34                                                               106.6 (4)   O.sub.1b C.sub.1b C.sub.2b                                                               112.8 (5)                                      N.sub.3 C.sub.34 C.sub.33                                                                110.2 (4)   O.sub.2b C.sub. 2b C.sub.1b                                                              112.6 (5)                                                            O.sub.1c C.sub.1c C.sub.2c                                                               114.9 (6)                                      ClNaC.sub.g1.sup.c                                                                        83.6 (-)   O.sub.2c C.sub.2c C.sub.1c                                                               121.1 (6)                                      ClNaO.sub.1b                                                                              89.5 (1)   C.sub.g1 NaO.sub.1b.sup.c                                                                111.1 (-)                                      ClNaO.sub.2b                                                                             156.0 (1)   C.sub.g1 NaO.sub.2b.sup.c                                                                110.2 (-)                                      ClNaO.sub.1c                                                                             108.2 (1)   C.sub.g1 NaO.sub.1c.sup.c                                                                 99.4 (-)                                      ClNaO.sub.2c                                                                              84.2 (1)   C.sub.g1 NaO.sub.2c.sup.c                                                                155.9 (-)                                      ClNaN.sub.1                                                                               61.5 (1)   O.sub.1b NaO.sub.2b                                                                       67.4 (2)                                      ClNaN.sub.11                                                                              73.3 (2)   O.sub.1b NaO.sub.1c                                                                      146.4 (2)                                      ClNaC.sub.12                                                                             100.0 (2)   O.sub.1b NaO.sub.2c                                                                       89.4 (2)                                      ClNaC.sub.13                                                                             104.4 (2)   O.sub.2b NaO.sub.1c                                                                       89.3 (2)                                      ClNaC.sub.14                                                                              81.1 (2)   O.sub.2b NaO.sub.2c                                                                       88.8 (2)                                                            O.sub.1c NaO.sub.2c                                                                       65.1 (2)                                      N.sub.1 NaC.sub.11                                                                       25.9 (2)                                                             N.sub.1 NaC.sub.14                                                                       25.5 (2)    N.sub.1 NaC.sub.12                                                                       43.8 (2)                                       C.sub.11 NaC.sub.12                                                                      27.0 (2)    N.sub.1 NaC.sub.13                                                                       43.3 (2)                                       C.sub.12 NaC.sub.13                                                                      26.9 (2)    C.sub.11 NaC.sub.13                                                                      43.5 (2)                                       C.sub.13 NaC.sub.14                                                                      25.9 (2)    C.sub.12 NaC.sub.14                                                                      42.9 (2)                                                             C.sub.11 NaC.sub.14                                                                      41.9 (2)                                       ______________________________________                                          .sup.a The numbers in parentheses are the estimated standard deviations i      the last significant digit.                                                    .sup.b Atoms are labeled in agreement with FIG. 7.                             .sup.c The symbol C.sub.g1 is used to designate the center of gravity for      the fivemembered ring containing N.sub.1, C.sub.11, C.sub.12, C.sub.13,        and C.sub.14 ; this value is therefore listed without an estimated             standard deviation.                                                      

While this invention has been described in detail for the purpose of illustration, it is not to be construed as limited thereby but is intended to cover all changes and modifications within the spirit and scope thereof. 

That which is claimed is:
 1. A composition comprising Cr₅ (C₄ H₄ N)₁₀ (C₄ H₈ O)₄.
 2. A composition comprising [Cr(C₄ H₄ N)₄ ].
 3. A composition comprising [Cr(C₄ H₄ N)₄ ][Na]₂.2(OC₄ H₈).
 4. A composition comprising [Cr(C₄ H₄ N)₅ (OC₄ H₈)].
 5. A composition comprising [Cr(C₄ H₄ N)₅ (OC₄ H₈)][Na]₂.4(OC₄ H₈).
 6. A process to prepare a chromium-containing compound comprising forming a mixture of and refluxing:(a) a chromium salt; (b) a metal amide; and (c) an electron pair donor solvent
 7. A process according to claim 6 wherein said chromium salt is selected from the group consisting of chromium acids, chromium halides, and mixtures thereof.
 8. A process according to claim 7 wherein said chromium salt is a chromium halide selected from the group consisting of chromous chloride, chromic chloride, and mixtures thereof.
 9. A process according to claim 6 wherein said metal amide is selected from the group consisting of alkali metal amide salt, alkaline earth metal amide salts, silyl amide salts, and mixtures thereof.
 10. A process according to claim 9 wherein said metal amide has from about 1 to about 20 carbon atoms per molecule.
 11. A process according to claim 6 wherein said metal amide is an unsaturated compound.
 12. A process according to claim 11 wherein said metal amide is an aromatic compound.
 13. A process according to claim 6 wherein said metal amide has amine ligand and wherein said amine ligand is selected from the group consisting of pyrrolide ligands, derivatives of pyrrole ligands, and mixtures thereof.
 14. A process according to claim 6 wherein said electron pair donor solvent has from about 2 to about 20 carbon atoms per molecule.
 15. A process according to claim 6 wherein said electron pair donor solvent is an aliphatic compound.
 16. A process according to claim 6 wherein said metal amide is soluble in said electron pair donor solvent.
 17. A process according to claim 6 wherein said electron pair donor solvent is an ether and is selected from the group consisting of tetrahydrofuran, derivatives of tetrahydrofuran, dimethoxyethane, derivatives of dimethoxyethane, and mixtures thereof.
 18. A process according to claim 6 wherein said mixture is maintained in a liquid state.
 19. A process according to claim 18 wherein said mixture is maintained in a liquid state for a time in the range of about 1 minute to about 1 week.
 20. A process according to claim 6 wherein said liquid is filtered to remove any reaction by-products.
 21. A process according to claim 20 wherein the thus-filtered liquid is treated to form a solid.
 22. A process according to claim 21 wherein the thus-filtered liquid is slowly evaporated.
 23. A process according to claim 21 wherein the thus-filtered liquid is treated with a non-polar solvent.
 24. A process according to claim 22 wherein a solid is recovered.
 25. A process according to claim 23 wherein a solid is recovered.
 26. A process to prepare one or more chromium-containing compound comprising forming a mixture of and refluxing:(a) about one mole of chromous chloride; (b) about two moles of sodium pyrrole; and (c) tetrahydrofuran
 27. A process to prepare one or more chromium-containing compounds comprising forming a mixture of and refluxing:(a) about one mole of chromous chloride; (b) an excess of sodium pyrrole; and (c) an excess of tetrahydrofuran.
 28. A process to prepare one or more chromium-containing compounds comprising forming a reaction mixture of and refluxing:(a) about one mole of chromic chloride; (b) about three moles of sodium pyrrole; and (c) an excess of dimethoxyethane.
 29. A process to prepare one or more chromium-containing compounds comprising forming a mixture of:(a) about one mole of chromous chloride; (b) an excess of dimethyl pyrrole; and (c) an excess of tetrahydrofuran.
 30. A process according to claim 26 wherein one or more compounds are recovered.
 31. A process according to claim 27 wherein one or more compounds are recovered.
 32. A process according to claim 28 wherein one or more compounds are recovered.
 33. A process according to claim 29 wherein one or more compounds are recovered.
 34. A composition comprising Cr(NC₄ H₄)₃ Cl(O₂ C₂ H₄ (CH₃)₂).
 35. A composition comprising Cr(NC₄ H₄)₃ Cl(O₂ C₂ H₄ (CH₃)₂)₃ Na.
 36. A process according to claim 13 wherein said chromium-containing compound is a chromium pyrrolide. 